Understanding the influence of iron impurity on the formation of the structure and the properties of hypereutectic aluminum-silicon alloys are important for achieving the required quality of castings, especially those obtained from secondary materials. In the present work, the influence of different iron contents (0.3, 1.1, and 2.0 wt.%) on the crystallization process, microstructure and mechanical properties of the Al-15% Si alloy was studied. It is shown that the presence of iron impurity in the Al-15% Si alloy leads to increasing the eutectic crystallization time from 6.2 to 7.6 s at increasing the iron content from 0.3 wt.% to 1.1 wt.%, changing the structure of the alloy eutectic in the solid state. The primary silicon and β-Al5SiFe phase coexist in the structure of the Al-15% Si alloys at a temperature below 575 °C in the range of iron concentrations from 0 to 2 wt.% in equilibrium conditions. In the experimental alloys structure, the primary crystals of the β-phase were metallographically detected only in the alloys containing 1.1 and 2 wt.% of iron impurity. Increase of the iron content up to 2 wt.% significantly reduces the mechanical properties of the Al-15% Si alloy due to the formation of large platelet-like inclusions of β-Al5SiFe phase.

The series of experiments was performed on commercial polymeric composite material MultimetalStahl 1018. Strength tests were performed to determine the yield point of the material. The composite had the highest hardness at a temperature of 20°C. Hardness and microhardness were determined in further experiments. The adhesiveness of the material to metal surfaces and impact strength were also analyzed. The scanning electron microscopy and X-ray microanalysis methods were used for analyzing the microstructure of the material. Chemical composition of selected areas was analyzed, which allowed for a preliminary identification of metallic elements content in the composite. The microstructure of composite is highly non-homogeneous and particular phases are highly elongated and angular. The analyzed phase was enriched with silicon, aluminium, magnesium, iron and vanadium other phases enriched with metallic elements, e.g. molybdenum, titanium, vanadium and also oxygen as well as traces of cadmium and chromium. The results were presented in the form of photos and illustrations. The results confirmed the applicability of the composite as a binder for fixing mechanical and foundry devices.

The study presents a concept of generation of micro-cracks (or cracks) in metal specimens in order to assess their material with respect to the thermal shock resistance. Both the method of conducting the experiment and the criteria of the assessment of the material resistance to the rapid temperature changes are discussed. The schematic diagram of the research stand used for repeated heating and rapid cooling of specimens, constructed in the Foundry Institute of the Częstochowa University of Technology, is presented. The proposed solution enables to maintain constant conditions of the experiment. The tests were held for flat specimens 70 mm long, 20 mm wide, and 5 mm thick, tapered over a distance of 15 mm towards both ends. The specimens were induction heated up to the specified temperature and then, in response to the signal produced by a pyrometer, dipped in the tank containing the cooling medium. The thermal shock resistance of the material can be assessed on the basis of either the total length of the micro-cracks arisen at the tapered parts of a specimen after a specified number of heating-and-cooling cycles, or the number of such cycles prior to the total damage of a specimen, or else the number of thermal cycles prior to generation of the first crack. The study includes an exemplary view of the metal specimen after the thermal shock resistance tests, as well as the illustrative microstructure of the vermicular cast iron which reveals a crack propagating from the edge towards the core of the material.

Production waste is one of the major sources of aluminium for recycling. Depending on the waste sources, it can be directly melted in furnaces, pre-cleaned and then melted, or due to the small size of the material (powder or dust) left without remelting. The latter form of waste includes chips formed during mechanical cutting (sawing) of aluminium and its alloys. In this study, this type of chips (with the dimensions not exceeding 1 mm) were melted. The obtained results of laboratory tests have indicated that even chips of such small sizes pressed into cylindrical compacts can be remelted. The high recovery yield (up to 94 %) and degree of metal coalescence (up to 100 %) were achieved via thermal removal of impurities under controlled conditions of a gas atmosphere (argon or/and air), followed with consolidation of chips at a pressure of minimum 170 MPa and melting at 750 oC with NaCl-KCl-Na3AlF6 salt flux.

The paper discusses issues related to the technology of melting and processing of copper alloys. An assessment was made of the impact of titanium and iron introduced in the form of pre-alloy - Ti73Fe master alloy on the microstructure and selected properties of pure copper and copper-silicon alloy. There are known examples of the use of titanium and iron additive to the copper alloy. Titanium as an additive introduced to copper alloys to improve their properties is sometimes also applicable. In the first stage of the study, a series of experimental castings were conducted with variable content of Ti73Fe master alloy entering copper in quantities of 5 %, 15 %, 25 % in relation to the mass of the metal charge. In the second stage, a silicon additive was introduced into copper in the amount of about 4 % by weight and 0.5 % and 1 % respectively of the initial Ti73Fe alloy. Thermodynamic phase parameters were modelled using CALPHAD method and Thermo-Calc software, thus obtaining the crystallization characteristics of the test alloys and the percentage of structural components at ambient temperature. Experiments confirmed the validity of the use of Ti73Fe master alloy as an additive. The pre-alloy used showed a favourable performance, both in terms of addition solubility and in the area of improvement of strength properties. Changes were achieved in the microstructure, mainly within the grain, but also in the developed dendrites of the solid solution. Changes occur with the introduction of titanium with iron into copper as well as to two-component silicon bronze.