With the use of differential scanning calorimetry (DSC), the characteristic temperatures and enthalpy of phase transformations were
defined for commercial AlSi9Cu3 cast alloy (EN AC-46000) that is being used for example for pressurized castings for automotive
industry. During the heating with the speed of 10oCmin-1
two endothermic effects has been observed. The first appears at the temperature
between 495 oC and 534 oC, and the other between 555 oC and 631 oC. With these reactions the phase transformation enthalpy comes up as
+6 J g-1
and +327 J g-1
. During the cooling with the same speed, three endothermic reactions were observed at the temperatures between
584 oC and 471 oC. The total enthalpy of the transitions is – 348 J g-1
.
Complimentary to the calorimetric research, the structural tests (SEM and EDX) were conducted on light microscope Reichert and on
scanning microscope Hitachi S-4200. As it comes out of that, there are dendrites in the structure of α(Al) solution, as well as the eutectic
(β) silicon crystals, and two types of eutectic mixture: double eutectic α(Al)+β(Si) and compound eutectic α+Al2Cu+β.