Abstract

The paper presents results of calorimetric studies of foundry nickel superalloys: IN100, IN713C, Mar - M247 and ŻS6 U. Particular attention was paid to determination of phase transiti ons temperatures during heating and cooling. The samples were heated to a temperature of 1500°C with a rate of 10°C ⋅ min – 1 and then held at this temperature for 5 min. After a complete melting, the samples were cooled with the same rat e. Argon with a purity of 99.99% constituted the protective atmosphere. The sample was placed in an alundum crucible with a capacity of 0.45 cm 3 . Temperature and heat calibration was carried out based on the mel ting point of high- purity Ni. The tests were carried out by the differential scanning calorimetry (DSC) using a Multi HTC high -temperature calorimeter from Setaram. Based on the DSC curves, the following temperatures were determined: solidus and liquidus, dissolution and precipitation of the γ ’ phase, MC carbides and melting of the γ ’ /γ eutectic. In the temperature range of 100 -1100°C, specific heat capacity of the investigated superalloys was determined. It was found that the IN713C and IN100 alloys exhibit a higher specific heat while compared to the Mar - M247 and ŻS6 U alloys.

Go to article

Authors and Affiliations

R. Przeliorz
J. Piątkowski

This page uses 'cookies'. Learn more