The influence of sewage sludge torrefaction temperature on fuel properties was investigated. Non-lignocellulosic waste thermal treatment experiment was conducted within 1 h residence time, under the following temperatures: 200, 220, 240, 260, 280 and 300°C. Sawdust was used as lignocellulosic reference material. The following parameters of biochar have been measured: moisture, higher heating value, ash content, volatile compounds and sulfur content. Sawdust biochar has been confirmed to be a good quality solid fuel. High ash and sulfur content may be an obstacle for biochar energy reuse. The best temperature profile for sawdust torrefaction and fuel production for 1 h residence time was 220°C. At this temperature the product contained 84% of initial energy while decreased the mass by 25%. The best temperature profile for sewage sludge was 240°C. The energy residue was 91% and the mass residue was 85%. Higher temperatures in both cases caused excessive mass and energy losses.

Anaerobic digestion residue represents a nutrient rich resource which, if applied back on land, can reduce the use of mineral fertilizers and improve soil fertility. However, dewatering and further thermal processing of digestate may be recommended in certain situations. Limited applicability of digestate as fertilizer may appear, especially in winter, during the vegetation period or in areas where advanced eutrophication of arable land and water bodies is developing. The use of digestate may be also governed by different laws depending on whether it is treated as fertilizer, sewage sludge or waste. The aim of this paper is to present the effects of thermal treatment of solid fraction of digestate by drying followed by pyrolysis and gasification. Pyrolysis was carried out at the temperature of about 500°C. During this process the composition of flammable gases was checked and their calorific value was assessed. Then, a comparative analysis of energy parameters of the digestate and the carbonizate was performed. Gasification of digestate was carried out at the temperature of about 850°C with use of CO2 as the gasifi cation agent. Gasification produced gas with higher calorific value than pyrolysis, but carbonizate from pyrolysis had good properties to be used as a solid fuel