The paper presents the results of comparative tests of the fatigue properties conducted on two non-ferrous alloys designated as Al 6082 and
Al 7075 which, due to the satisfactory functional characteristics, are widely used as engineering materials. The fatigue tests were carried
out using a proprietary, modified low cycle test (MLCF). Particular attention was paid to the fatigue strength exponent b and fatigue
ductility exponent c. Based on the tests carried out, the results comprised within the range defined by the literature were obtained. These
results prove a satisfactory sensitivity of the method applied, its efficiency, the possibility of conducting tests in a fully economical way
and above all the reliability of the obtained results of the measurements. Thus, the thesis has been justified that the modified low cycle
fatigue test (MLCF) can be recommended as a tool used in the development of alloy characteristics within the range of low-cycle variable
loads
In this study, the mechanical tests were carried out on ductile iron of EN-GJS-600-3 grade and on grey cast iron of EN-GJL-250 grade. The fatigue life was evaluated in a modified low-cycle fatigue test (MLCF), which enables the determination of parameters resulting from the Manson-Coffin-Morrow relationship. The qualitative and quantitative metallographic studies conducted by light microscopy on selected samples of ductile iron with spheroidal graphite and grey cast iron with lamellar graphite (showing only small variations in mechanical properties,) confirmed also small variations in the geometrical parameters of graphite related with its content and morphological features.