The widespread use of Fibre-Reinforced Polymers (FRP) reinforced concrete (RC) structural members is hindered by their low fire resistant characteristics, limiting their use to cases, where fire resistance is not a priority. Presented and discussed are experimental results pertaining to the flexural members subjected to heating and simultaneous loading. Solely non-metallic FRP bars: (i) Basalt FRP (BFRP), (ii) Hybrid FRP (HFRP) with carbon and basalt fibres and (ii) nano-Hybrid FRP (nHFRP) with modified epoxy resin, were used as internal reinforcement for beams. The destruction of the beams was caused in different ways, beams reinforced with BFRP bars were destroyed by reinforcement failure while those reinforced with hybrid FRP bars were destroyed by concrete crushing. The BFRP reinforced beams obtained a maximum temperature, measured directly on the bars, of 917 °C, compared to beams reinforced with hybrid FRP bars, where the temperature on the bars reached 400-550 °C at failure. Moreover, the highest registered ductility was obtained for BFRP reinforced beams as well, where the maximum deflections reached approximately 16 cm.
The paper describes the recent developments of Hybrid Fibre-Reinforced Polymer (HFRP) and nano-Hybrid Fibre-Reinforced Polymer (nHFRP) bars. Hybridization of less expensive basalt fibres with carbon fibres leads to more sustainable alternative to Basalt-FRP (BFRP) bars and more economically-efficient alternative to Carbon-FRP (CFRP) bars. The New-Developed HFRP bars were subjected to tensile axial loading to investigate its structural behaviour. The effect of hybridization on tensile properties of HFRP bars was verified experimentally by comparing the results of tensile test of HFRP bars with non-hybrid BFRP bars. It is worth to mention that the difference in obtained strength characteristics between analytical and numerical considerations was very small, however the obtained results were much higher than results obtained experimentally. Authors suggested that lower results obtained experimentally can be explained by imperfect interphase development and therefore attempted to improve the chemical cohesion between constituents by adding nanosilica particles to matrix consistency.