In the latest period hundreds of concrete viaducts were built in Poland within a short time range. The cases of destruction of concrete road viaducts described by the author in the article concern in the construction of such structures in various parts of our country, such as central regions of Poland, Warmia-Masuria, south – east - a total of about 30 objects. The occurring phenomenon is related to the micro cracks of the cement matrix which are not visible on the surface of the elements and become visible only after the cyclic freezing process as a result of the standard F150 frost resistance test, the so-called the standard method according to Annex N to the PN-B-06265: 2018 standard. The destruction took an unprecedented course and aroused much discussion in the scientific community. This article summarizes this discussion and indicates the root cause of the destruction.

The article discusses the physical and chemical mechanisms of the carbonation phenomenon itself, as well as points out the synergistic effect of frost destruction and concrete carbonation on reinforced concrete elements. Examples of structural damage from engineering practice in the diagnosis of reinforced concrete structures are presented. Two cases of frost and carbonation damage of precast reinforced concrete elements are analyzed. It was noted that the most common cause of damage to concrete structures is the lack of frost resistance. Carbonation of concrete leads to deprivation of the protective properties of the concrete lagging against the reinforcing steel. The examples cited include precast elements that, for technical reasons, had a relatively small lagging thickness. The first one relates to the thin walled elevation elements, which are exploited during 60 years and the second relates to the energetic poles with very advanced concrete corrosion damage. The examples given of corrosion of concrete and reinforcement of elements indicate that synergistic environmental interactions can intensify the destruction of elements.