Measurements of the hardening process of the selected self-setting sands are presented in the hereby paper. Moulding sands were prepared

on the matrix of „Szczakowa” sand of the Sibelco Company. Two resins: phenol-formaldehyde-furfuryl (FF/AF) and urea-formaldehydefurfuryl

(MF/AF) were used for making moulding sands. – Methylbenzene-sulphonic acid was applied as a hardener for the moulding sand

on FF/AF resin, while paratoluene-sulphonic acid for the moulding sand on MF/AF resin. Both hardeners were used in two concentrations:

low – the so-called ‘slow’ hardener and high - ‘fast’ hardener. During investigations, the courses of the hardening process were

determined, more accurately changes of the velocity of the ultrasound wave passage through the moulding sand cL = f(t) and changes of

the moulding sand hardening degree versus time, Sx = f(t). In addition, the kinetics of the hardening process was determined.

Measurements were performed on the research stand for ultrasound investigations.

Measurements of the hardening process course of the selected self-hardening moulding sands with the reclaimed material additions to the matrix, are presented in the hereby paper. Moulding sands were produced on the „Szczakowa” sand (of the Sibelco Company) as the matrix of the main fraction FG 0,40/0,32/0,20, while the reclaim was added to it in amounts of 20, 50 and 70%. Regeneration was performed with a horizontal mechanical regenerator capacity of 10 t/h. In addition, two moulding sands, one on the fresh sand matrix another on the reclaimed matrix, were prepared for comparison. Highly-fluid urea-furfuryl resin was used as a binder, while paratoluensulphonic acid as a hardener. During investigations the hardening process course was determined, it means the wave velocity change in time: cL = f(t). The hardening process kinetics was also assessed (dClx/dt = f(t)). Investigations were carried out on the research stand for ultrasound tests. In addition strength tests were performed.