The article presents research results of the strength parameters of HPC achieved in various research conditions. The research was carried out on substantially different samples, both as to the size as the slenderness ratio. Moreover, the assessment of the effect of speed of a load on strength parameters as well as other factors which in a significant way show the difference in the strength values was made. For comparison, the results were also applied to the relations known in ordinary concrete.

This paper addresses the tensile and flexural strength of HPC (high performance concrete). The aim of the paper is to analyse the efficiency of models proposed in different codes. In particular, three design procedures from: the ACI 318 [1], Eurocode 2 [2] and the Model Code 2010 [3] are considered. The associations between design tensile strength of concrete obtained from these three codes and compressive strength are compared with experimental results of tensile strength and flexural strength by statistical tools. Experimental results of tensile strength were obtained in the splitting test. Based on this comparison, conclusions are drawn according to the fit between the design methods and the test data. The comparison shows that tensile strength and flexural strength of HPC depend on more influential factors and not only compressive strength.

The paper presents the results of experimental investigations performed by the authors on the casting position factor. It was proved that at the height of reinforced concrete elements there are different bond conditions. Moreover, the bond depends on concrete mechanical properties, element height as well as concrete mix composition and consistency. The experiments also showed the advisability of determining the casting position factor separately for bars from normal concrete and those from high–performance concrete (HPC). The analysis of investigation results has shown that “good” bond conditions are a relative concept and depend on, among other things, element height. The higher the element the better the concrete to lower bars bond. Consequently, elements of considerable height (higher than 600 mm) demonstrate a bigger difference between concrete to upper bars bond and concrete to lower bars bond.

This paper presents the details of optimized mix design for normal strength and high performance concrete using particle packing method. A critical review of mix design methods have been carried out for normal strength concrete using American Concrete Institute (ACI) and Bureau of Indian Standards (BIS) methods highlighting the similarities and differences towards attaining a particular design compressive strength. Mix design for M30 and M40 grades of concrete have been carried out using ACI, BIS and particle packing methods. Optimization of concrete mix has been carried out by means of particle packing method using EMMA software, which employs modified Anderson curve to adjust the main proportions. Compressive strength is evaluated for the adjusted proportions and it is observed that the mixes designed by particle packing method estimates compressive strength closer to design compressive strength. Further, particle packing method has been employed to optimize the ingredients of high performance concrete and experiments have been carried out to check the design adequacy of the desired concrete compressive strength.

The ductility of High Performance Concrete (HPC) can develop both in tension and compression.This aspect is evidenced in the present paper by measuring the mechanical response of normalvibrated concrete (NC), self-compacting concrete (SC) and some HPCs cylindrical specimensunder uniaxial and triaxial compression. The post-peak behaviour of these specimens is definedby a non-dimensional function that relates the inelastic displacement and the relative stress duringsoftening. Both for NC and SC, the increase of the fracture toughness with the confinement stressis observed. Conversely, all the tested HPCs, even in absence of confinement, show practically thesame ductility measured in normal and self-compacting concretes with a confining pressure. Thus,the presence of HPC in compressed columns is itself sufficient to create a sort of active distributedconfinement.

In the recent years a tendency for design of increasingly slender structures with the use of high performance concrete has been observed. Moreover, the use of high performance concrete in tunnel structures, subject to high loads with possibility of extreme loads occurrence such as fire, has an increasing significance. Presented studies aimed at improving high performance concrete properties in high temperature conditions (close to fire conditions) by aeration process, and determining high temperature impact on the concretes features related to their durability. In this paper it has been proven that it is possible to obtain high performance concretes resistant to high temperatures, and additionally that modification of the concrete mix with aerating additive does not result in deterioration of concrete properties when subject to water impact in various form.

In recent years, carbon fibres have been extensively used to strengthen concrete structures. In most cases, the lamination process is carried out using epoxy resin as matrix. In some cases, especially when strengthen structural elements made of weak concrete, it is possible to replace the epoxy resin with an inorganic, cement matrix, while at the same time maintaining a sufficient efficiency of strengthen understood as the percentage increase in the compressive strength of concrete samples due to the applied reinforcement in relation to the reference concrete. In these studies, elements of carbon fibres mats that are reinforced with a cement matrix were used as the starting product for fibre recovery. The laminate, which was used to reinforce concrete elements, was detached from the concrete surface and subjected to processing in order to obtain clean carbon fibre scraps without cement matrix. Then, the obtained carbon material, in shaped form, was used to strengthen self-compacting, high performance, fibre reinforced concrete (SCHPFRC). For comparative purposes, this concrete was also strengthened by carbon fibre mats (with one and three layers of CFRP). Each samples were tested in uniaxial compression test. The compressive strength of concrete reinforced with 1 and 3 layers of CFRP was higher by 37.9 and 96.3%, respectively, compared to the reference concrete. On the other hand, the compressive strength of concrete reinforced with 1 and 3 layers of carbon fibre scrapswas higher by 11.8 and 40.1%, respectively. Regardless of the reinforcement technique used, the composite elements showed a higher deformability limit in comparison plain concrete. The obtained results showed that it is possible to reuse carbon fibre to strengthen structural elements made of SCHPFRC effectively, using simple processing methods.

Continuous steel-concrete composite girder can fully utilize material strength and possess large spanning ability for bridge constructions. However, the weak cracking resistance at the negative bending moment region of the girder seriously harms its durability and serviceability. This paper investigates practical techniques to improve the cracking performance of continuous steel-concrete composite girders subjected to hogging moment.Areal continuous girderwas selected as the background bridge and introduced for numerical analysis. Modeling results show that under the serviceability limit state, the principle stress of concrete slabs near the middle piers of the bridgewas far beyond the allowable material strength, producing a maximum tensile stress of 10.0 MPa. Approaches for strengthening concrete decks at the negative moment region were developed and the effectiveness of each approach was assessed by examing the tensile stress in the slabs. Results indicate that the temporary counterweight approach decreased the maximum tensile stress in concrete slabs by 22%. Due to concrete shrinkage and creep, more than 65% of the prestressed compressive stresses in concrete slabs were finally dispersed to the steel beams. A thin ultra-high performance concrete (UHPC) overlay at the hogging moment region effectively increased the cracking resistance of the slabs, and practical engineering results convicted the applicability of the UHPC technique.

This study provides a comparative analysis of natural nanosilica (NSn), which is an extract of natural silica sand processed into nanosilica with commercial nanosilica (NSc) derived from semiconductor industrial waste, in 80 MPa high performance concrete (HPC). The percentage of using nanosilica is (3%, 5%, 10%, 15%) by weight of cement used directly and combined with 5% silica fume. Analysis was carried out through compressive strength test, durability through permeability test, rapid chloride penetration test (RCPT), and microstructure test through scanning electron microscopy (SEM). The results of the analysis show that natural nanosilica is equivalent to commercial nanosilica, in applications it is better to use silica fume incorporation. The optimum percentage of using NSn10% and (SF) 5%, while 5% NSc and 5% SF, in these proportions shows the best compressive strength and durability. It’s just that the use of natural nanosilika is 5% more than commercial nanosilika. The benefit of this research is that natural materials such as silica sand with high SiO2 content, can be processed into nanosilica as an advanced material, which can be used as an eco-friendly construction material.