In the dissertation it has been shown, that so called “time-thermal treatment” (TTT) of the alloy in liquid state as overheating the metal

with around 250o

C above Tliq. and detailing it in temperature for 30 to 40 minutes has the influence on changing the crystallization

parameters (Tliq., TEmin.

, TEmax., TE(Me), TSol.). It was ascertained, that overheating the AlSi17Cu5Mg alloy substantially above Tliq. results

with microcrystalline structure. Evenly distributed in the eutectic warp primeval silicon crystals and supersaturated with alloying additives

of base content (Cu, Mg, Fe) of α(Al) solution, ensures not only increase durability in ambient temperature, but also at elevated

temperature (250o

C), what due to it’s use in car industry is an advantage.

In the dissertation it has been shown, that so called „time-thermal treatment” (TTT) of the alloy in liquid state, as overheating the metal

with around 250o

C above the Tliq. and detaining it in this temperature for around 30 minutes, improves the mechanical properties (HB, Rm,

R0,2). It was ascertained, that overheating the AlSi17Cu5Mg alloy aids the modification, resulting with microcrystalline structure. Uniform

arrangement of the Si primeval crystals in the warp, and α(Al) solution type, supersaturated with alloying elements present in the base

content (Cu, Mg) assures not only increased durability in the ambient temperature, but also at elevated temperature (250o

C), what is an

advantage, especially due to the use in car industry.

The paper presents the results of studies on the effect of the AlSi17Cu5 alloy overheating to atemperature of 920°C and modification with phosphorus (CuP10) on the resultingmechanical (HB, Rm, R0.2) and plastic (A5 and Z) properties. It has been shown that, so-called, "timethermal treatment" (TTT) of an alloy in the liquid state, consisting inoverheating the metal to about 250°C above Tliq,holding at this temperature by 30 minutes improvesthe mechanical properties. It has also been found that overheating of alloy above Tliq.enhances the process of modification, resulting in the formation of fine-grain structure. The primary silicon crystals uniformly distributed in the eutectic and characteristics ofthe α(Al) solution supersaturated with alloying elements present in the starting alloy composition (Cu, Fe) provide not only an increase of strength at ambient temperature but also at elevated temperature (250°C).