Abstract

In this paper, explain the preparation of CaTiO3 ceramics synthesized by the solid-state reaction method. Calcium carbonate and titanium dioxide were high energy mixed in stoichiometric amounts, and the obtained mixture was calcined at different temperatures (800, 900, 1000 and 1300ºC) for 2 h. The obtained samples were characterized by measurement of particle size, Energy Dispersive X-Ray (EDX) Analysis; differential thermal analysis, X-ray diffraction and SEM images. XRD patterns indicated that CaTiO3 ceramics with the structure of perovskite is obtained from calcined powders at 1,300°C for 2 h. SEM images show the formation of a very fine and homogeneous morphology. The measured values of electrical resistivity were within the typical range of insulating materials and approach values corresponding to insulating ceramics.

Go to article

Authors and Affiliations

E. Rocha-Rangel
J. López-Hernández
J.A. Castillo-Martínez
J.J. Osorio-Ramos
C.A. Calles-Arriaga
I. Estrada-Guel
R. Martínez-Sánchez
Download PDF Download RIS Download Bibtex

Abstract

A SrTiO3 electroceramic with perovskite structure was produced by the calcination of a mixture of SrCO3 and TiO2 intensively grounded by high energy milling. For this purpose, raw materials were mixed in stoichiometric amounts in a planetary type mill; the obtained powder mixture was calcined for 2 h at temperatures between 800 and 1300°C. Samples resulting from the calcination were characterized by XRD, FTIR, SEM analysis and electrical measurements. From XRD, it was determined that the SrTiO3 formed presents the cubic structure of perovskite. The complete reaction for SrTiO3 compound formation occurs at 1200°C. Micrograph observations indicate the presence of a homogeneous microstructure with tiny grain size. The measured values of electrical resistivity were within the typical range of insulating materials.

Go to article

Authors and Affiliations

Enrique Rocha-Rangel
ORCID: ORCID
Wilian J. Pech-Rodríguez
Juan López-Hernández
ORCID: ORCID
Carlos A. Calles-Arriaga
ORCID: ORCID
Eddie N. Armendáriz-Mireles
José A. Castillo-Robles
José A. Rodríguez-García
ORCID: ORCID

This page uses 'cookies'. Learn more