Brazing of two dissimilar structural materials; Zircaloy-4 and SS-316L was performed at 900oC under high vacuum conditions. The metallic glass ribbons (Zr55Cu30Al10Ni2Fe3-at. %) of 30 µm thickness, were used as an interlayer. The bonded region was characterized by scanning electron microscope (SEM), energy dispersive spectroscope (EDS) and microhardness testing. The metallurgical bond formation was due to compositional changes in the molten interlayer and later on its subsequent solidification. Assessment of the bonded zone (BZ) revealed three distinct regions (Region-I, Region-II and Region-III). Diffusion transformation was observed in Region-I and Region-III which were interface with base alloys SS-316L and Zircaloy-4 respectively. However, Region-II at the middle of the BZ was composed of isothermally and athermally solidified portions. The highest values of Microhardness were observed in Region-III which was due to the presence of hard phases. Moreover, a crack parallel to BZ was observed in Region-III and was attributed to differential contraction of base alloys during cooling. Maximum shear stress acting on the BZ was calculated and correlated to the brittle phase cracking.
In the past few years, overhead copper transmission lines have been replaced by lightweight aluminum transmission lines to minimize the cost and prevent the sagging of heavier copper transmission lines. High strength aluminum alloys are used as the core of the overhead transmission lines because of the low strength of the conductor line. However, alloying copper with aluminum causes a reduction in electrical conductivity due to the solid solution of each component. Therefore, in this study, the authors attempt to study the effect of various Al/Cu ratios (9:1, 7:3, 5:5) to obtain a high strength Al-Cu alloy without a significant loss in its conductivity through powder metallurgy. Low-temperature extrusion of Al/Cu powder was done at 350ºC to minimize the alloying reactions. The as-extruded microstructure was analyzed and various phases (Cu9Al4, CuAl2) were determined. The tensile strength and electrical conductivity of different mixing ratios of Al and Cu powders were studied. The results suggest that the tensile strength of samples is improved considerably while the conductivity falls slightly but lies within the limits of applications.
Iron is the most common and detrimental impurity in casting alloys and has been associated with many defects. The main consequence of
the presence or adding of iron to AlSi alloys is the formation Fe-rich intermetallics with especially deleterious β-Al5FeSi. β-Al5FeSi phases
are most often called needles on 2D micro sections, whilst platelets in 3D geometry. The x-ray tomography results have demonstrated Ferich
phases with shapes different from simple forms such as needles or platelets and presented bent and branched phases. β grown as
complicated structure of bent and branched intermetallics can decrease feeding ability, strengthen pores nucleation and eutectic colonies
nucleation leading to lower permeability of mushy zone and porosity in the castings.
Solidification of AlSiFe alloys was studied using a directional solidification facility and the CALPHAD technique was applied to calculate
phase diagrams and to predict occurring phases. The specimens solidified by electromagnetic stirring showed segregation across, and the
measured chemical compositions were transferred into phase diagrams. The ternary phase diagrams presented different solidification paths
caused by segregation in each selected specimen. The property diagrams showed modification in the sequence and precipitation
temperature of the phases. It is proposed in the study to use thermodynamic calculations with Thermo-Calc which enables us to visualize
the mushy zone in directional solidification. 2D maps based on property diagrams show a mushy zone with a liquid channel in the
AlSi7Fe1.0 specimen center, where significant mass fraction (33%) of β-Al5FeSi phases may precipitate before α-Al dendrites form.
Otherwise liquid channel occurred almost empty of β in AlSi7Fe0.5 specimen and completely without β in AlSi9Fe0.2. The property
diagrams revealed also possible formation of α–Al8Fe2Si phases.
This paper aims to investigate the microstructural evolution and mechanical properties of hot-deformed AlMg4 alloys with Mn, Fe, and Si as the main impurities. For this purpose, solidification behavior and microstructural evolution during hot-rolling and heat-treatment processes are investigated by using theoretical calculations and experimental characterization. The crystallization and morphological transformation of intermetallic Al3Fe, Al6Mn, and Mg2Si phases are revealed and discussed in terms of the variation in chemical composition. Following a homogenization heat-treatment, the effect of heat treatment on the intermetallic compounds is also investigated after hot-rolling. It was revealed that the Mg2Si phase can be broken into small particles and spherodized more easily than the Al3Fe intermetallic phase during the hot-rolling process. For the Mn containing alloys, both yield and ultimate tensile strength of the hot-rolled alloys increased from 270 to 296 MPa while elongation decreased from 17 to 13%, which can be attributed to Mn-containing intermetallic as well as dispersoid.
Al2Cu phase has been obtained by melting pure metals in the electric arc furnace. It has been found that the intermetallic phase undergoes selective corrosion in the H3PO4 aqueous solutions. Aluminium is dissolved, the surface becomes porous and enriched with copper. The corrosion rate equals to 371 ± 17 g·m–2·day–1 (aerated solution) and 284 ± 9 g·m–2·day–1 (deaerated solution). The surface of Al2Cu phase after selective corrosion was characterised by using electrochemical impedance spectroscopy. It was found that the surface area of the specimens increases with temperature due to higher corrosion rate and is between 2137 and 3896 cm2.
Sodium orthovanadate was tested as a corrosion inhibitor of intermetallic Al2Cu in 1 M H3PO4. The Al2Cu – H3PO4 – Na3VO4 system was studied using the following methods: inductively coupled plasma optical emission spectrometry, scanning electron microscopy with energy dispersive x-ray spectroscopy, x-ray diffraction, electrochemical impedance spectroscopy, polarisation and open circuit potential. It was found that the corrosion rate decreased as the inhibitor concentration increased. The highest inhibition efficiency 99% was obtained when sodium orthovanadate initial concentration was equal to 100 mM, pH = 1.11, due to precipitation of a protective layer of insoluble salt, containing vanadium, phosphorus, sodium and oxygen, on the surface. At pH = 0.76 the protective layer was not formed and inhibition efficiency decreased to 76%. Selective corrosion of the intermetallic phase caused a significant increase of an electric double layer capacitance and decrease of a charge transfer resistance.
Understanding the influence of iron impurity on the formation of the structure and the properties of hypereutectic aluminum-silicon alloys are important for achieving the required quality of castings, especially those obtained from secondary materials. In the present work, the influence of different iron contents (0.3, 1.1, and 2.0 wt.%) on the crystallization process, microstructure and mechanical properties of the Al-15% Si alloy was studied. It is shown that the presence of iron impurity in the Al-15% Si alloy leads to increasing the eutectic crystallization time from 6.2 to 7.6 s at increasing the iron content from 0.3 wt.% to 1.1 wt.%, changing the structure of the alloy eutectic in the solid state. The primary silicon and β-Al5SiFe phase coexist in the structure of the Al-15% Si alloys at a temperature below 575 °C in the range of iron concentrations from 0 to 2 wt.% in equilibrium conditions. In the experimental alloys structure, the primary crystals of the β-phase were metallographically detected only in the alloys containing 1.1 and 2 wt.% of iron impurity. Increase of the iron content up to 2 wt.% significantly reduces the mechanical properties of the Al-15% Si alloy due to the formation of large platelet-like inclusions of β-Al5SiFe phase.
This article deals with the effect of manganese that is the most applied element to eliminate the negative effect of iron in the investigated alloy AlSi7Mg0.3. In this time are several methods that are used for elimination harmful effect of iron. The most used method is elimination by applying the additive elements, so-called iron correctors. The influence of manganese on the morphology of excluded ironbased intermetallic phases was analysed at various iron contents (0.4; 0.8 and 1.2 wt. %). The effect of manganese was assessed in additions of 0.1; 0.2; 0.4 and 0.6 wt. % Mn. The morphology of iron intermetallic phases was assessed using electron microscopy (SEM) and EDX analysis. The increase of iron content in investigated alloys caused the formation of more intermetallic phases and this effect has been more significant with higher concentrations of manganese. The measurements carried out also showed that alloys with the same Mn/Fe ratio can manifest different structures and characteristics of excluded iron-based intermetallic phases, which might, at the same time, be related to different resulting mechanical properties.
The paper presents an analysis of a selected grade of high silicon cast iron intended for work in corrosive and abrasive conditions. The text describes its microstructure taking into account the process of crystallization, TDA analysis, EDS, XRD and the chemical composition analysis. In order to determine the phase composition, X-ray diffraction tests were carried out. The tests were executed on a Panalytical X'Pert PRO X-ray diffractometer with filtration of radiation from a lamp with copper anode and PIXcel 3D detector on the deflected beam axis. Completed tests allowed to describe the microstructure with detailed consideration of intermetallic phases present in the alloy. Results of the analysis of the examined alloy clearly show that we deal with intermetallic phases of Fe3Si, Fe5Si3 types, as well as silicon ferrite and crystals of silicon. In the examined alloy, we observed the phenomenon of segregation of carbon, which, as a result of this process, enriches the surface of silicon crystals, not creating a compound with it. Moreover, the paper demonstrates capability for crystallization of spheroidal graphite in the examined alloy despite lack of elements that contribute to balling in the charge materials.