The investigation was carried out on forest soils collected from areas subject to variable pollution. The fraction of strontium was analyzed in soil samples from north-eastern Poland (Borki forest division), treated as a non-polluted region (natural background) and in soil samples from central (Rogów forest division) and south-western Poland (Świerklaniec forest division). The sequential extraction procedure was applied in this study to separate the fractions of strontium. Five fractions were analyzed in every genetic horizon according to the Tessier method. The concentration of strontium was also analyzed in the plants. Both results were compared in order to evaluate the mobility and bioavailability of the trace elements in the environment. The content, distribution and bioavailability of the strontium fractions were investigated with particular emphasis on the contaminated study sites. Total content of strontium in surface horizons depended on the localization. Among analysed fractions strontium, in organic soil horizons, regardless of localization, occurred predominantly in mobile fractions in all examined soils.

To investigate the adsorptive properties of a local laterite deposited in Chenzhou, Hunan province, China, the adsorptive properties of the natural laterite were investigated by batch technique in this study. The effects of contact time, pH, ionic strength, temperature, and the concentration on adsorption properties were also analyzed. The obtained experimental results show that the main mineral composition of laterite is kaolinite and montmorillonite. The adsorption process achieved equilibrium within 60 minutes and 90 minutes for Sr(II) and Cr(VI), respectively. The adsorption capacities for Cr(VI) and Sr(II) by the laterite were about 7.25 mg·g^-1 and 8.35 mg·g^-1 under the given experimental conditions, respectively. The equilibrium adsorption data were fitted to the second-order kinetic equation. The adsorption capacity for Sr(II) onto the laterite increased with increasing pH from 3–11 but decreased with increasing ionic strength from 0.001 to 1.0 M NaCl. The Sr(II) adsorption reaction on laterite was endothermic and the process of adsorption was favored at high temperature. Similarly, the adsorption capacity for Cr(VI) onto the laterite increased with increasing pH from 3–11, however, the ionic strength and temperature had an insignificant effect on Cr(VI) adsorption. The adsorption of Cr(VI) and Sr(II) was dominated by ion exchange and surface complexation in this work. Furthermore, the Langmuir and Freundlich adsorption isotherm model was used for the description of the adsorption process. The results suggest that the studied laterite samples can be effectively used for the treatment of contaminated wastewaters.

Main aim of submitted work is evaluation and experimental verification of inoculation effect on Al alloys hot-tear sensitivity. Submitted work consists of two parts. The first part introduces the reader to the hot tearing in general and provides theoretical analysis of hot tearing phenomenon. The second part describes strontium effect on hot tearing susceptibility, and gives the results on hot tearing for various aluminium alloys. During the test, the effect of alloy chemical composition on hot tearing susceptibility was also analyzed. Two different Al-based alloys were examined. Conclusions deals with effect of strontium on hot tearing susceptibility and confirms that main objective was achieved.

This article deal with non-conventional methods to affect the crystallization of Al-alloys by the application of electromagnetic field. The application of electromagnetic field is not technically complicated, it does not require mechanical contact with the melt, and the scale of the crystallization influence is not dependent on the thickness of the casting. Two experimental materials were used: AlSi10MgMn and AlSi8Cu2Mn and two values of electromagnetic induction: B = 0.1 T a B = 0.2 T. The best results for alloy AlSi10MgMn were achieved by application of electromagnetic field with induction B = 0.2 T; during this experiment the best mechanical properties were achieved - the biggest increase of mechanical properties was recorded. The best results for alloy AlSi8Cu2Mn were achieved by combination of electromagnetic field with induction B = 0.1 T and modification by 0.05 wt. % Sr. In this case we don´t recommend to use electromagnetic field with induction B = 0.2 T; because of deposition of coarse grains and decreasing of mechanical properties.

The paper concerns the processes connected with the formation of chromium white cast iron microstructure. The influence of titanium and strontium on the alloy crystallization has been described using TDA method and EDS analysis. Conducted experiments allowed the determination of the selected additions influence on the microstructure of examined alloys. TDA analysis enabled indication of the characteristic temperatures of thermal effects for samples with strontium and titanium and the comparison of results for the reference sample without additions. The results of TDA test also included the analysis of the temperature first derivative values, which presented interesting differences as well. The scanning microscopy observation clearly indicated the difference between the effect of strontium and titanium on the alloy microstructure. The EDS analysis helped to identify the chemical composition of the evolving phases and confirmed the strontium presence in the eutectic. Experimental results allowed to draw reliable conclusions about the effect of applied additions on the crystallization and microstructure of chromium cast iron.

With the aid of eutectic modification treatment, the precipitation of coarse lamellar eutectic silicon can be suspended during the solidification of aluminum-silicon alloys, thereby the formation of fine-grained, fibrous eutectic Si can be promoted by the addition of small amounts of modifying elements, such as Sr, to the liquid alloy. The effectiveness of this technique is, however, highly dependent on many technological factors, and the degree of modification can be lowered during the various stages of melt preparation due to the oxidation of the Sr-content of the melt. During our research, we investigated the effect of rotary degassing melt treatments coupled with the addition of three different fluxes on the degree of modification of an Al-Si-Mg-Cu casting alloy. It was also studied, that whether additional Sr alloying made before and during the melt treatments can compensate the Sr fading with time. The degree of eutectic modification was characterized by thermal analysis (TA) and the microscopic investigation of TA specimens. It was found, that by using one of the three fluxes, and by adding Sr master alloy rods before the melt treatments, better modification levels could be achieved. It was also found that the measurement of Sr-concentration by optical emission spectroscopy alone cannot be used for controlling the level of eutectic modification.

Metal ions can modify plant metabolism and change the level of biologically active components. In the present study, the impact of short-term exposure to strontium on the accumulation of the metal as well as the content of isoflavones in soybean sprouts was investigated.

The seeds were germinated in hydroponics with 0, 1, 1.5, 2.5, 5.0, or 10.0 mM of Sr for 72 hours. The content of strontium was assessed using flame atomic absorption spectrometry and the amount of isoflavones was determined with high performance liquid chromatography. Dose-dependent accumulation of Sr and a linear correlation between the Sr concentration in the growth medium and the content of the element in the plant samples were observed. The largest changes in the isoflavone content, compared to the control, were noted in soy sprouts germinated in the presence of 5 and 10 mM of strontium. Daidzin, genistin, malonyldaidzin, and malonylgenistin were the dominant isoflavones and their content increased by approx. 28, 44, 34, and 47%, respectively, compared to the control. Low amounts of aglycones were found; moreover, their content decreased by ca. 19–30%. Our research can be important for obtaining a natural product enhanced with strontium and isoflavones, which contribute to prevention of osteoporosis associated with endogenous oestrogen deficits.

In this work, we developed the lanthanum strontium cobalt ferrite and it’s composite with yttrium iron cobaltite (mass ratio of 1:1) cathodes as a thin layer on Ce0.8Sm0.2O1.9 electrolyte. Two kinds of electrode pastes were prepared, with and without 6 mm polystyrene beads as an additional pore former. The performance of cathode materials was investigated by electrochemical impedance spectroscopy as a function of electrode morphology, oxygen partial pressure, potential, and temperature. The polarization resistance of the more porous electrodes was lower than those electrodes prepared without additional pore former in the whole potential range at 800°C, slightly lower at 700°C and 600°C. The addition of yttrium iron cobaltite decreased the performance of both types of cathodes. The lower polarization resistance of porous cathodes is due to the facilitated gas diffusion through their structure.