Internal casting defects that are detected by radiography may also be detected by ultrasonic method. Ultrasonic testing allows investigation of the cross-sectional area of a casting, it is considered to be a volumetric inspection method. The high frequency acoustic energy travels through the casting until it hits the opposite surface or an interface or defect. The interface or defect reflects portions of the energy, which are collected in a receiving unit and displayed for the analyst to view. The pattern of the energy deflection can indicate internal defect. Ultrasonic casting testing is very complicated in practice. The complications are mainly due to the coarse-grain structure of the casting that causes a high ultrasound attenuation. High attenuation then makes it impossible to test the entire volume of material. This article is focused on measurement of attenuation, the effect of probe frequency on attenuation and testing results.

The article deals with ultrasonic testing possibilities of the copper alloy centrifugal casts. It focused on the problems that arise when testing

of castings is made of non-ferrous materials. Most common types of casting defects is dedicated in theoretical introduction of article.

Ultrasonic testing technique by conventional ultrasound system is described in the theoretical part too. Practical ultrasonic testing of

centrifugal copper alloy cast - brass is in experimental part. The experimental sample was part of centrifugally cast brass ring with

dimensions of Ø1200x34 mm. The influence of microstructure on ultrasonic attenuation and limitations in testing due to attenuation is

describes in experimental part. Conventional direct single element contact ultrasound probe with frequencies of 5 MHz, 3.5 MHz and 2

MHz were used for all experimental measurements. The results of experimental part of article are recommendations for selecting

equipment and accessories for casting testing made of non-ferrous metals.