Abstract

This paper presents the study of microstructure and properties of 8 mol% yttrium stabilized zirconia coating fabricated by Plasma Spray Physical Vapor Deposition technique on commercial pure titanium. The coating was characterized by X-ray diffraction, high resolution scanning electron microscope, profilometer, nanoindentation and nanomachining tests. The X-ray phase analysis exhibit the tetragonal Zr0.935Y0.065O1.968, TiO and α-Ti phases. The Rietveld refinement technique were indicated the changes of crystal structure of the produced coatings. The characteristic structure of columns were observed in High Resolutions Scanning Electron Microscopy. Moreover, the obtained coating had various development of surfaces, thickness was equal to 3.1(1) µm and roughness 0.40(7) µm. Furthermore, the production coatings did not show microcracks, delamination and crumbing. The performed experiment encourages carried out us to tests for osseointegration.

Go to article

Authors and Affiliations

J. Barczyk
G. Dercz
I. Matuła
M. Góral
J. Maszybrocka
D. Bochenek
W. Gurdziel
Download PDF Download RIS Download Bibtex

Abstract

In this study T6 heat treated 6063 aluminum alloys were used as substrate material. In order to form a bond between the substrate and the

main coating, all samples were coated with Ni-Cr-Al powders. 8 wt% Yttria Stabilized Zirconia powders (YSZ) were coated with plasma

spray technique. Thickness of YSZ was 150 m and bond coating was 36 m. XRD and SEM-EDS analyses were performed to characterize

the coating layers. These YSZ coated and uncoated samples were subjected to wear testing under different spindle speed, loading and

working distance. Wear test results were compared with the kinetic friction coefficients and weight loss values. Wear marks on YSZ

coated and uncoated samples were investigated by SEM analysis. By coating with plasma spray technique, the wear resistance of Al alloys

was increased without changing the friction coefficient. It was found that spindle speed had significant effect over the wear properties than

the load applied. By YSZ coating, wear properties were increased 10 times.

Go to article