This paper concerns the possibility of use the Jiles-Atherton extended model to describe the magnetic characteristics of construction steel St3 under mechanical stress. Results of the modelling utilizing extended Jiles-Atherton model are consistent with results of experimental measurements for magnetic hysteresis loops B(H). Material stress state determination by using non-destructive, magnetic properties based on testing techniques is an especially important problem.

The work presents the results of the research and tests of the surface machining of the S355NL and X5CrNi18-10 steels with the concentraded stream of heat with the usage of the GTAW method. The surface layers of the tested steels were remelted with the electric arc using the current of the electric arc 50, 100, 150 and 200A.The machining was done in the atmosphere of argon with the constant speed of the welding head. A microscope examination was performed of the obtained structure and measurements of depth, width and hardness of the received surface layer were performed. Moreover the relation between the current of the electric arc and geometry of the remelted layers with their microhardness was examined.

This study investigates mechanical properties of accelerated cooled and self-tempered (AC-ST) H-type S275JR quality steel sections in HEA120 and HEB120 sizes. The cooling process is conducted with a specially manufactured system that sprays a coolant consisting of a water + compressed air mixture on the section surfaces. Cooling times were applied as 10 and 30 seconds using 4 and 12 bar compressed air + water at an average constant pressure of 5 bar and a constant flow rate of 0.08 kg/s. In the HEA120 sections, the highest cooling rate was obtained with 83°C/s in the web region under the cooling time of 30 s and the air pressure cooling condition of 12 bar. At the cooling rate up to 6°C/s, the microstructure is transformed to acicular ferrite and polygonal ferrite phase from Ferrite+Pearlite. But upper bainite phase was formed at a cooling rate of 30°C/s, and a small amount of martensite and lower bainite microstructures were observed at a cooling rate of 60°C/s and above. The hardness in the untreated sections, in the range of 106-120 HB, was increased to 195 HB at a cooling rate of 83 C/s in the web region of the HEA120 section. For a cooling rate of 23°C/s, the maximum compressive residual stresses of –352 MPa are measured in the crotch region of the HEB120. And for a cooling rate of 6°C/s, the maximum tensile residual stresses of 442 MPa were determined in the flange region of the HEA120 section.