A study was undertaken to investigate the effects of crumb rubber on the strength and mechanical behaviour of Rubberized cement soil (RCS). In the present investigation, 26 groups of soil samples were prepared at five different percentages of crumb rubber content, four different percentages of cement content and two different finenesses of crumb rubber particle. Compressive strength tests were carried out at the curing age of 7 days, 14 days, 28 days and 90 days. The test results indicated that the inclusion of crumb rubber within cement soil leads to a decrease in the compressive strength and stiffness and improves the cement soil’s brittle behaviour to a more ductile one. A reduction of up to 31% in the compressive strength happened in the 20% crumb content group. The compressive strength increases with the increase in the cement content. And the enlargement of cement content is more efficient at low cement content.

The objective of the presented paper is to investigate the performance of concrete containing volcanic scoria as cement replacement after 7, 28, 90, and 180 days curing. Five performance indicators have been studied. Compressive strength, water permeability, porosity, chloride penetrability, and reinforcement corrosion resistance have all been evaluated. Concrete specimens were produced with replacement levels ranging from 10 to 35%. Test results revealed that curing time had a large influence on all the examined performance indicators of scoria-based concrete. Water permeability, porosity, and chloride penetrability of scoria-based concrete mixes were much lower than that of plain concrete. Concretes produced with scoria-based binders also decelerated rebar corrosion, particularly after longer curing times. Furthermore, an estimation equation has been developed by the authors to predict the studied performance indicators, focusing on the curing time and the replacement level of volcanic scoria. SEM/EDX analysis has been reported as well.