Rare earth metals including yttrium and europium are one of several critical raw materials, the use of which ensures the development of the so-called high technology. The possibility of their recovery in Europe is limited practically only to secondary materials such as phosphogypsum and electronic waste.

The article presents the results of our research concerning the development of recovery technology of yttrium and europium from luminophore CRT used lamps. It describes the principle of separation of elements and the test results of cleaning the concentrate. It was shown that the costs of preparing the concentrate according to the proposed technology are lower than the phosphogypsum processing technology and the composition of the resulting product does not contain hazardous substances.

In the present paper the structure and thermal properties of europium cerium oxides were investigated. The material for the research was obtained via solid state synthesis. The initial powders: ceria CeO2 and europia Eu2O3 were mixed in 1:1 mass ratio (non-stoichiometric proportion with the excess of CeO2) and milled. The sintering process was performed using high temperature vacuum press at 1350°C. Calorimetric analysis was conducted both for initial powders and milled mixture. The structure, phase composition and thermal diffusivity of obtained material were investigated in as-sintered condition. It was revealed that the obtained material was multi-phase. Non-stoichiometric phases including Ce0.5Eu0.5O1.75 with fluorite type structure and different lattice parameters were present. Thermal diffusivity decreased in the range from 25 to 900°C from 1.49 to 0.57 mm2/s and then increased to 0.70 mm2/s at 1400°C.

In the article, the characterization of the microstructure, phase composition and distribution of elements in the Eu2O3-ZrO2 sintered materials obtained by four different ways of powders’ homogenization (mixing) process and different temperature of sintering process is shown. The feedstock powders with an average mole ratio of ZrO2 to Eu2O3 equal 74% to 26% were used as an initial material. The principal aim of the investigation was characterization of differences in the microstructure of the same type of ceramics, however, prepared via different mixing and manufacturing processes. The range of the investigation covered a characterization of these materials via phase identification of all samples by XRD (X-ray diffraction) and characterization of internal morphology of the specimens with detailed analysis of elements distributions by SEM (scanning electron microscopy) and EDS (energy dispersive spectrometry). The aim of the following investigation is to characterize the possibilities of the solid state synthesis of the europium zirconate based materials, dedicated for TBC applications.

In this paper an analysis of the surface properties of (Ti,Pd,Eu)O_x thin films prepared by magnetron sputtering has been described. In particular, the results of composition and structure investigations were studied in relation to the surface state and optical properties. It was found that (Ti,Pd,Eu)O_x film was nanocrystalline and had a rutile structure. The average crystallites size was equal to 7.8 nm. Films were homogeneous and had densely packed grains. Investigation of the surface properties by XPS showed that titanium was present at 4+ state (in the TiO₂form), palladium occurred as PdO₂(also at 4+ state), while europium was in Eu₂O₃form (at 3+ state). In comparison with the unmodiffied TiO₂, the coating with Pd and Eu additives had a rather high transparency (approx. 47%) in the visible light range, its optical absorption edge was shifted towards into the longer wavelengths (from 345 nm to 452 nm), and the width of optical energy gap Egopt was nearly twice lower (1.82 eV). Besides, the resistivity of (Ti,Pd,Eu)O_x at room temperature was 1×10³ Wcm. In the case of the film as-deposited on Si substrate (p-type) the generation of photocurrent as a response to light beam excitation (λ_exc = 527 nm) was observed.