The morphology of G20Mn5 specimens made of non-modified and rare earth metals (REM) modified cast steel was investigated. Molten metal was treated with a cerium-rich mischmetal contain 49.8% Ce, 21.8% La, 17.1% Nd, 5.5% Pr and 5.35% other rare earth metals making up the balance. The melting, quenching (920°C/water) and tempering (720°C/air) were performed under industrial conditions. Analysis included G20Mn5 cast steel fracture specimens subjected to Charpy V-notch impact testing at 20°C, -30°C and -40°C. The purpose of the analysis was to determine the influence of REM on the microstructure and mechanical properties of G20Mn5 cast steel and the REM effect on the morphology, impact strength and character of the fracture surfaces. In addition, a description of the mechanism by which fracture occurred in the two materials was proposed. The author demonstrated the beneficial effects of adding REM to molten steel, manifested by a 20 - 40% increase in impact toughness, depending on test temperature, as compared to the non-modified cast steel. Important findings included more than 100% increase in impact strength in comparison with the required impact toughness of 27J at -40C for heat treated steels (EN 10213).

The article presents the results of research concerning AlCu4MgSi alloy ingots produced using horizontal continuous casting process under variable conditions of casting speed and cooling liquid flow through the crystallizer. The mechanical properties and structure of the obtained ingots were correlated with the process parameters. On the basis of the obtained results, it has been shown that depending on the cooling rate and the intensity of convection during solidification, significant differences in the mechanical properties and structure and of the ingots can occur. The research has shown that, as the casting speed and the flow rate of the cooling liquid increase, the hardness of the test samples decreases, while their elongation increases, which is related to the increase of the average grain size. Also, the morphology of the intermetallic phases precipitations lattice, as well as the centerline porosity and dendrite expansion, significantly affect the tensile strength and fracture mechanism of the tested ingots.