The authors studied the fracture mechanical properties under half-symmetric loading in this paper. The stress distribution around the crack tip and the stress intensity factor of three kinds of notched specimens under half symmetric loading were compared. The maximum tensile stress σmax of double notch specimens was much greater than that of single notch specimens and the maximum shear stress τmax was almost equal, which means that the single notch specimens were more prone to Mode II fractures. The intensity factors KII of central notch specimens were very small compared with other specimens and they induced Mode I fractures. For both double notch and single notch specimens, KII was kept at a constant level and did not change with the change of a/h, and KII was much larger than KI. KII has the potential to reach its fracture toughness KIIC before KI and Mode II fractures occurred. Rock-like materials were introduced to produce single notch specimens. Test results show that the crack had been initiated at the crack tip and propagated along the original notch face, and a Mode II fracture occurred. There was no relationship between the peak load and the original notch length. The average value of KIIC was about 0.602 MPa×m1/2, and KIIC was about 3.8 times KIC. The half symmetric loading test of single notch specimens was one of the most effective methods to obtain a true Mode II fracture and determine Mode fracture toughness.
The ductility of High Performance Concrete (HPC) can develop both in tension and compression.This aspect is evidenced in the present paper by measuring the mechanical response of normalvibrated concrete (NC), self-compacting concrete (SC) and some HPCs cylindrical specimensunder uniaxial and triaxial compression. The post-peak behaviour of these specimens is definedby a non-dimensional function that relates the inelastic displacement and the relative stress duringsoftening. Both for NC and SC, the increase of the fracture toughness with the confinement stressis observed. Conversely, all the tested HPCs, even in absence of confinement, show practically thesame ductility measured in normal and self-compacting concretes with a confining pressure. Thus,the presence of HPC in compressed columns is itself sufficient to create a sort of active distributedconfinement.
New graphite tools were designed and produced to fabricate a semi-finished product from which nine cutting inserts were obtained in one spark plasma sintering process. As a result, WC-5Co cemented carbides were spark plasma sintered and the effect of various sintering parameters such as compacting pressure, heating rate and holding time on the main mechanical properties were investigated. It was shown that WC-5Co cemented carbides spark plasma sintered at 1200°C, 80 MPa, 400°C/min, for 5 min are characterized by the best relation of hardness (1861 ±10 HV30) and fracture toughness (9.30 MPa·m1/2). The microstructure of these materials besides the WC ceramic phase and Co binder phase consists of a synthesized Co3W3C complex phase. Comparison with a commercial WC-6Co cutting insert fabricated by conventional powder metallurgy techniques shows that spark plasma sintering is a very effective technique to produce materials characterized by improved mechanical properties.
Wider application of silicon carbide (SiC) is anticipated for increasing the durability of various structural facilities. For this study, SiC was fabricated with decreased electrical resistivity for precision electrical discharge machining. Two-step reaction sintering by infiltration of molten Fe-Si alloy was applied for SiC fabrication. The procedure included first sintering at 973 K in Ar gas atmosphere and second sintering by spontaneous infiltration of molten Fe-75%Si alloy at 1693 K in vacuum. The sintered structure porosity became very low, forming 3C-type SiC. Results confirmed that molten Fe-75%Si alloy infiltration occurred because of reaction sintering. The electrical resistivity of the sintered SiC infiltrated by molten Fe-75%Si alloy can be improved to be two orders of magnitude lower than that by molten Si, consequently maintaining the high performance of SiC.
The paper deals with the properties and microstructure of Reactive Powder Concrete (RPC), which was developed at Cracow University of Technology. The influence of three different curing conditions: water (W), steam (S) and autoclave (A) and also steel fibres content on selected properties of RPC was analyzed. The composite characterized by w/s ratio equal to 0.20 and silica fume to cement ratio 20%, depending on curing conditions and fibres content, obtained compressive strength was in the range from 200 to 315 MPa, while modulus of elasticity determined during compression was about 50 GPa. During three-point bending test load-deflection curves were registered. Base on aforementioned measurements following parameters were calculated: flexural strength, stress at limit of proportionality (LOP), stress at modulus of rapture (MOR), work of fracture (WF), and toughness indices I₅, I₁₀ and I₂₀. Both amount of steel fibres and curing conditions influence the deflection of RPC during bending.