Nitrogen-doped DLC (diamond-like carbon) coatings were produced on 316L nitrided austenitic steel in direct current and pulsed glow discharge conditions. The chemical composition, surface topography, hardness and corrosion resistance of the obtained carbon coatings were examined. The coatings varied in surface morphology, roughness and hardness. Direct current glow discharge made it possible to produce a coating characterized by lower hardness, greater thickness and higher nitrogen content. The coating featured improved corrosion resistance and adhesion compared to coatings produced in the pulsed process.

Deep cryogenic treatment (DCT) is gaining popularity as a treatment used to modify structures obtained during heat or thermo-chemical treatment. The article presents the influence of DCT, carried out during heat treatment before and after gas nitriding processes, on the formation of gas nitrided layers on X153CrMoV12 steel. It was found that the use of DCT between quenching and tempering performed prior to gas nitriding processes, increases the hardness, thickness and wear resistance of the nitrided layers. At the same time, if we apply cryogenic treatment during post-heat treatment of nitrided layers, we also get very high wear resistance and increased thickness of nitrided layers, in comparison with conventional gas nitriding of X153CrMoV12 steel. In this case, DCT significantly increases also the hardness of the core by the transformation of retained austenite and the precipitation of fine carbides of alloying elements.