The subject of the study was the No. 116/2 coal seam belonging to the Cracow Sandstone Series of the Upper Silesian Coal Basin. Reflectograms of the samples taking into account all the vitrinite group macerals present in the coal were recorded for Δ R^o close to the standard deviation and in the standard range. A careful analysis of vitrinite reflectograms reveals the presence of three or four clearly distinguished peaks. When assessing the rank of coal, only the main maximum, peak No. 4, was considered to be significant. Measurements of the average reflectance of collotelinite were made only on the vitrinite surfaces with a thickness of more than 1 mm. Only two maxima were revealed on detailed reflectograms. These maxima correlate with the peaks marked as No. 3 and 4 in the sample reflectograms taking into account all the vitrinite group macerals. The C ^daf content in the tested coal from the Janina coal mine is between 75.9 and 77.5 wt%, while for vitrain, it ranges from 71.1 to 75.5 wt%. This relationship is an exponential regression with a correlation coefficient of r = 0.95h and can be approximated by a linear correlation of r = 0.94. The correlation strength between the volatile matter content and the coefficient of average reflectance in the vitrinite of the tested coal was also examined. The statistically significant correlation is strong, which is expressed by the exponential correlation coefficient “r” being close to 0.99 and its linear approximation with the correlation coefficient r = 0.98. However, no correlation was found between the measured reflectance values and the GI coefficient calculated for the examined samples.

Studies on the quality of bituminous coal are mainly focused on physico-chemical analysis, examining the ash content, sulphur content, volatile matter content, moisture content, and the Net Calorific Value of coal. Until now, the above mentioned parameters form the basis of the Polish Standard PN-82/87002, on the basis of which individual types of bituminous coal are determined. In addition, an elemental analysis, providing information about the content of primary elements in the organic matter of solids, i.e. coal, hydrogen, nitrogen, oxygen, and sulphur, is carried out for the selected samples. This issue has been studied by many authors, which undoubtedly provide invaluable knowledge due to the huge amount of data, but, as the authors themselves indicate, the knowledge of the petrography of coal, coking properties (Probierz et al. 2012) and finally the coke obtained from individual coal types (based on tests carried out using the Karbotest installation or the so-called „box tests” performed in the coke oven battery) is still very limited. The article discusses the impact of petrographic composition on the quality of metallurgical coke. The analysis was performed using samples of coking coal from the following mines: Pniówek, Zofiówka, Borynia, and Krupiński. The mentioned coal types are used to produce coke mixtures used for the production of coke in the Przyjaźń and Radlin coking plants. Based on the rank of coal and physicochemical parameters, the mentioned coal types were classified according to the Polish classification and the UN/ECE International Classification of In-Seam Coals (UN/ECE 1995). The prediction of thermomechanical properties of coke (CSR and CRI) performed according to the original CCP method were compared with the results obtained using the classical method of Nippon Steel Corporation.