In this paper, the influence of Mo addition on the structure and mechanical properties of the NiCoMnIn alloys have been studied. Series of polycrystalline NiCoMnIn alloys containing from 0 to 5 mas.% of Mo were produced by the arc melting technique. For the alloys containing Mo, two-phase microstructure was observed. Mo-rich precipitates were distributed randomly in the matrix. The relative volume fraction of the precipitates depends on the Mo content. The numbers of the Mo rich precipitates increases with the Mo contents. The structures of the phases were determined by the TEM. The mechanical properties of the alloys are strongly affected by Mo addition contents. Brittleness of the alloys increases with the Mo contents.
Shape memory alloys are characterised by interesting properties, i.e. shape memory effect and pseudoelasticity, which enable their increasing application. Thermomechanical aspects of martensitic and reverse transformations in TiNi shape memory alloy subjected to tension tests were investigated. The stress-strain characteristics obtained during the tests were completed by the temperature characteristics. The temperature changes were calculated on the basis of thermograms determined by an infrared camera. Taking advantages from the infrared technique, the temperature distributions on the specimen’s surface were found. Heterogeneous temperature distributions, related to the nucleation and development of the new martensite phase, were registered and analysed. A significant temperature increase, up to 30 K, was registered during the martensitic transformation. The similar effects of the heterogeneous temperature distribution were observed during unloading, while the reverse transformation, martensite into austenite took place, accompanied by significant temperature decrease.
Cu-Al-based high temperature shape memory alloys are preferred commonly due to their cheap costs and shape memory properties. In recent years, studies have been conducted on developing and producing a new type of Cu-Al based shape memory alloy. In this study, the CuAl-Cr alloy system, which has never been produced before, is investigated. After production, the SEMEDX measurements were made in order to determine the phases in the Cu84–xAl12Crx+4 (x = 0, 4, 6) (weight %) alloy system; and precipitate phases together with martensite phases were detected in the alloys. The confirmations of these phases were made via x-ray measurements. The same phases were observed by XRD diffractogram of the alloys as well. The values of transformation temperature of alloys were determined with Differential Scanning Calorimetry (DSC) at 20°C/min heating rate. According to the DSC results, the transformation temperature of the alloys varies between 320°C and 350°C. This reveals that the alloys show high temperature shape memory characteristics.
The article presents a constitutive model for Shape Memory Alloys (SMA) along with result of dynamic simulations of SMA model. The applications of devices incorporating SMA in civil engineering focus mostly on mitigation of the seismic hazard effects in new-build and historical buildings or improvement of fatigue resilience. The unique properties of SMA, such as shape memory effect and superelasticity give promising results for such applications. The presented model includes additional phenomenon of SMA – internal loops. The paper shows the method of formulation of physical relations of SMA based on special rheological structure, which includes modified Kepes’s model. This rheological element, introduced as dual-phase plasticity body, is given in the context of martensite phase transformation. One of the advantages of such an approach is a possibility of formulation of constitutive relationships as a set of explicit differential equations. The application of the model is demonstrated on example of dynamic simulations of three dimensional finite element subjected to dynamic excitation.
In the present study, the corrosion behaviors of amorphous-nanocrystalline Ni50Ti50 shape memory alloy with different crystallite sizes were investigated. The Ni50Ti50 homogenized specimens were hot rolled and annealed at 950°C. Thereafter, the nanocrystalline Ni50Ti50 specimens with different crystalline sizes in the range of 40-350 nm were prepared by cold rolling and annealing at temperature range of 400 to 900oC. The corrosion resistance of Ni50Ti50 specimen with coarse grain size has significantly increased after cold rolling as a result of the formation of amorphous-nanocrystalline structure. The amorphous and nanocrystalline (with the crystallite size of about 40 nm) Ni50Ti50 samples exhibited the best corrosion resistance in the 5% HCl electrolyte with the corrosion potential and corrosion current density of about –197 mV and 2.34×10–6 A/cm2, respectively. This effect can be attributed to the higher density of crystalline defects in amorphous and nanocrystalline structures to quickly form protective films on the surface.
In this work, vacuum hot pressed Ni-Mn-Sn-In Heusler alloys with different concentration of In (0, 2 and 4 at.%), were investigated. The magneto-structural behaviour and microstructure dependencies on chemical composition and on heat treatment were examined. It was found that the martensite start transformation temperature increases with growing In content and to a lesser extent with increasing temperature of heat treatment. The high energy X-ray synchrotron radiation results, demonstrated that both chemical composition as well as temperature of heat treatment slightly modified the crystal structures of the studied alloys. Microstructural investigation performed by transmission electron microscopy confirmed chemical composition and crystal structure changes in the alloys.
In this study, a simple and effective way to fabricate highly porous scaffolds with controlled porosity and pore size is demonstrated. Ti-7Zr-6Sn-3Mo shape memory alloy fibers were prepared through a melt overflow process. The scaffolds with porosity of 65-85% and large pores of 100-700 μm in size were fabricated by sintering the as-solidified fibers. Microstructures and transformation behaviors of the porous scaffolds were investigated by means of SEM, DSC and XRD. The scaffolds were composed of β phase at room temperature. Superelasticity with the superelastic recovery strain of 7.4% was achieved by β↔α” phase transformation. An effect of porosity on mechanical properties of porous scaffolds was investigated by using compressive test. As the porosity increased from 65% to 85%, elastic modulus and compressive strength decreased from 0.95 to 0.06 GPa and from 27 to 2 MPa, respectively.