@ARTICLE{Keong_L.W._Wettability_2023,
 author={Keong, L.W. and Zainal, F.F. and Kasmuin, M.Z. and Mohamad, A.A. and Nazari, M.F.M. and Nabiałek, M. and Jeż, B.},
 volume={vol. 68},
 number={No 3},
 journal={Archives of Metallurgy and Materials},
 pages={1035-1040},
 howpublished={online},
 year={2023},
 publisher={Institute of Metallurgy and Materials Science of Polish Academy of Sciences},
 publisher={Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences},
 abstract={To fabricate a lead-free solder with better properties, a surface-modified precipitate calcium carbonate (PCC) was added as a reinforcement phase to tin-zinc (Sn-9Zn) solder. The surface modification of PCC was done by using electroless plating to deposit nickel (Ni) layer on the PCC. Based on microstructure analysis, a thin layer of Ni was detected on the reinforcement particle, indicating the Ni-coated PCC was successfully formed. Next, composite solder of Sn-9Zn-xNi-coated PCC (x = 0, 0.25, 0.50, 1.00 wt.%) was prepared. The morphology and phase changes of the composite solder were evaluated by using optical microscope and X-ray diffraction (XRD). Significant refinement on the grain size of Zn was seen with the additions of Ni-coated PCC, with a new phase of Ni3Sn4 was detected along with the phases of Sn and Zn. The wettability of Sn-9Zn was also improved with the presence of Ni-coated PCC, where the wetting angle decreased from 28.3° to 19.4-23.2°. Brinell hardness test revealed up to 27.9% increase in hardness for the composite solder than the pristine Sn-9Zn solder. This phenomenon contributed by the increased in dislocation resistance through Zener pinning effect and Zn grain refinement within the composite solder which enhanced the overall properties of the composite solder.},
 type={Article},
 title={Wettability and Hardness Investigation of Nickel-Coated Precipitated Calcium Carbonate Sn-9Zn Composite Solder},
 URL={http://journals.pan.pl/Content/128427/PDF-MASTER/AMM-2023-3-27-Nazeri.pdf},
 doi={10.24425/amm.2023.145472},
 keywords={Lead-free solder, Composite solder, Sn-9Zn, Precipitate calcium carbonate, Nickel coating},
}