TY - JOUR N2 - Castability of thin-walled castings is sensitive to variation in casting parameters. The variation in casting parameters can lead to undesired casting conditions which result in defect formation. Variation in rejection rate due to casting defect from one batch to other is common problem in foundries and the cause of this variation usually remain unknown due to complexity of the process. In this work, variation in casting parameters resulting from human involvement in the process is investigated. Casting practices of different groups of casting operators were evaluated and resulting variations in casting parameters were discussed. The effect of these variations was evaluated by comparing the rejection statistics for each group. In order to minimize process variation, optimized casting practices were implemented by developing specific process instructions for the operators. The significance of variation in casting parameters in terms of their impact on foundry rejections was evaluated by comparing the number of rejected components before and after implementation of optimized casting practices. It was concluded that variation in casting parameters due to variation in casting practices of different groups has significant impact on casting quality. Variation in mould temperature, melt temperature and pouring rate due to variation in handling time and practice resulted in varying quality of component from one batch to other. By implementing the optimized casting instruction, both quality and process reliability were improved significantly. L1 - http://journals.pan.pl/Content/103381/PDF/AFE%201_2018_19.pdf L2 - http://journals.pan.pl/Content/103381 PY - 2018 IS - No 1 KW - Investment casting KW - Casting defects KW - Process variations KW - Foundry practices A1 - Raza, M. A1 - Silva, P. A1 - Irwin, M. A1 - Fagerström, B. A1 - Jarfors, A.E.W. PB - The Katowice Branch of the Polish Academy of Sciences VL - vol.18 DA - 2018.03.20 T1 - Effects of Process Related Variations on Defect Formation in Investment Cast Components UR - http://journals.pan.pl/dlibra/publication/edition/103381 T2 - Archives of Foundry Engineering ER -