TY - JOUR N2 - Microstructure and texture of the CuCr0.6 alloy processed by rolling with cyclic movement of rolls (RCMR) at room temperature were investigated. The RCMR processing was applied for the samples in different initial conditions in the solid solution followed by quenching into iced water at 1000oC for 3 h and in aging treatment conditions performed at 500oC for 2 h and at 700oC for 24 h. Application of the solution and aging processes prior to RCMR deformation results in the partial dissolution of Cr particles into the Cu matrix and precipitation of the second phase particles. RCMR processing with value of the total effective strain (εft) of 5 was introduced to the material. It was found that the RCMR method is effective in texture weakening. The obtained results revealed that there is a large similarity in texture orientations after RCMR processing independently of heat treatment conditions. Cyclic character of deformation leads to an incomplete transition of LAB to HAB. L1 - http://journals.pan.pl/Content/113615/PDF/AMM-2019-4-46-Urbanczyk.pdf L2 - http://journals.pan.pl/Content/113615 PY - 2019 IS - No 4 EP - 1568 DO - 10.24425/amm.2019.130127 KW - severe plastic deformation KW - Heat treatment KW - Microstructure KW - Texture KW - CuCr0.6 alloy A1 - Urbańczyk-Gucwa, A. A1 - Brzezińska, A. A1 - Adamczyk-Cieślak, B. A1 - Rodak, K. PB - Institute of Metallurgy and Materials Science of Polish Academy of Sciences PB - Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences VL - vol. 64 DA - 2019.12.12 T1 - Crystallographic Texture and Grain Refinement in the CuCr Alloy Deformed by SPD Method SP - 1563 UR - http://journals.pan.pl/dlibra/publication/edition/113615 T2 - Archives of Metallurgy and Materials ER -