Rare earth Nd-Fe-B, a widely used magnet composition, was synthesized in a shape of powders using gas atomization, a rapid solidification based process. The microstructure and properties were investigated in accordance with solidification rate and densification. Detailed microstructural characterization was performed by using scanning electron microscope (SEM) and the structural properties were measured by using X-ray diffraction. Iron in the form of α-Fe phase was observed in powder of about 30 μm. It was expected that fraction of Nd2Fe14B phase increased rapidly with decrease in powder size, on the other hand that of α-Fe phase was decreased. Nd-rich phase diffused from grain boundary to particle boundary after hot deformation due to capillary action. The coercivity of the alloy decreased with increase in powder size. After hot deformation, Nd2Fe14B phase tend to align to c-axis.
NdFeB anisotropic sintered permanent magnets are typically fabricated by strip casting or melt spinning. In this study, the plastic deformability of an NdFeB alloy was investigated to study the possibility of fabricating anisotropic sintered magnets using gas atomized powders. The results show that the stoichiometric composition Nd12Fe82B6 softens at high temperatures. The aspect ratio and orientation factor of Nd12Fe82B6 billets after plastic deformation were found to increase with increasing plastic deformation temperature, particularly above 800℃. This confirms that softening at high temperatures can lead to plastic deformation of Nd2Fe14B hard magnetic phases.
Recently, since the demand of rare earth permanent magnet for high temperature applications such as an electric motor has increased, dysprosium (Dy), a heavy rare earth element, is becoming important due to severe bias in its production. To fulfill the increasing need of Dy, recycling offers as a promising alternative. In recycling of rare earths, Hydro-metallurgical extraction method is mainly used however it has adverse environmental effects. Liquid metal extraction on the other hand, is an eco-friendly and simple method as far as the reduction of rare earth metal oxide is concerned. Therefore, liquid metal extraction was studied in this research as an alternative to the hydro-metallurgical recycling method. Magnesium (Mg) is selected as solvent metal because it doesn’t form intermetallic compounds with Fe, B and has a low melting and low boiling point. Extraction behavior of Dy in (Nd,Dy)-Fe-B magnet is observed and effect of Mg ratio on extraction of Dy is confirmed.