The results of research on stereological parameters of carbides in modified hypoeutectic chromium cast iron were shown in the paper. The
effect of distance the casting heat centre of casting to the carbide phase morphology was examined. The samples for metallographic
examination were taken from various locations of the model casting prepared in a special tester. This model casting was designed to
simulate the solidification of heavy castings. Using the proposed methodology the relation of the distance from the model mould and the
size, perimeter, length, width and the shape factor of carbides was examined. During the analysis, the values of stereological parameters of
carbides changed on various sections of the model casting.
Paper presents the results of studies on primary crystallization and wear resistance of high chromium cast iron inoculated with
ferrotitanium intended for work in abrasive conditions. Primary crystallization was examined with use of TDA method, wear tests of the
samples were conducted using the modified pin-on-disk method.
The article shows results of studies of primary crystallization and wear resistance of Cr-Ni-Mo cast steel intended for work in corrosive
and abrasive conditions. The studies of primary crystallization were conducted with use of TDA method and modified tester allowing
measurement casting cooling time influence on the cooling and crystallization curves of studied alloys. After heat treatment of examined
cast steel wear tests of the samples were conducted on pin-on-disc type device.