In this study, high performance magnesium-yttria nanocomposite’s room temperature, strength and ductility were significantly enhanced by the dispersion of nano-sized nickel particles using powder blending and a microwave sintering process. The strengthening effect of the dispersed nano-sized nickel particles was consistent up to 100°C and then it gradually diminished with further increases in the test temperature. The ductility of the magnesium-yttria nanocomposite remained unaffected by the dispersed nano-sized nickel particles up to 100°C. Impressively, it was enhanced at 150°C and above, leading to the possibility of the near net shape fabrication of the nanocomposite at a significantly low temperature.
The addition of hard ceramic particles of nc-(Ti,Mo)C in carbon network into Ti matrix has been proved to be an efficient way to enhance their properties. The purpose of this work was to analyze the corrosion, tribological, mechanical and morphological effects of combining nc-(Ti,Mo)C/C with titanium metal, to create a unique composite via selective laser melting technique (SLM). Composites with different weight percentage (5, 10 and 20 wt %) of ceramic phase were produced. The samples of pure Ti and Ti-6Al-4V alloy were also tested, as a reference. These composites were examined for corrosion resistance in body fluid (artificial saliva solution). Moreover, the properties of titanium composites reinforced with nc-TiC powders were compared. It was stated that mechanical properties were significantly improved with increasing amount of nc-(Ti,Mo)C/C in Ti matrix. In terms of corrosion resistance, the composites showed worse properties compared to pure titanium and Ti-6Al-4V alloy, but better than TiC-reinforced composites.
Al-CuO is a thermite material exhibiting the exothermic reaction only when aluminum melts. For wide spread of its application, the reaction temperature needs to be reduced in addition to the enhancement of total reaction energy. In the present study, a thermite nanocomposite with a large contact area between Al and CuO was fabricated in order to lower the exothermic reaction temperature and to improve the reactivity. A cryomilling process was performed to achieve the nanostructure, and the effect of composition on the microstructure and its reactivity was studied in detail. The microstructure was characterized using SEM and XRD, and the thermal property was analyzed using DSC. The results show that as the molar ratio between Al and CuO varies, the fraction of uniform nanocomposite structure was changed affecting the exothermic reaction characteristics.
This work presents a theoretical study for the distribution of nanocomposite structure of plasmonic thin-film solar cells through the absorber layers. It can be reduced the material consumption and the cost of solar cell. Adding nanometallic fillers in the absorber layer has been improved optical, electrical characteristics and efficiency of traditional thin film solar cells (ITO /CdS/PbS/Al and SnO2/CdS/CdTe/Cu) models that using sub micro absorber layer. Also, this paper explains analysis of J-V, P-V and external quantum efficiency characteristics for nanocomposites thin film solar cell performance. Also, this paper presents the effect of increasing the concentration of nanofillers on the absorption, energy band gap and electron-hole generation rate of absorber layers and the effect of volume fraction on the energy conversion efficiency, fill factor, space charge region of the nanocomposites solar cells.
The paper presents the results of research on nanocomposite nickel/graphene oxide (Ni / GO) coatings produced by electrochemical reduction method on a steel substrate. Discussed is the method of manufacturing composite coatings with nickel matrix and embedded graphene oxide flakes. For comparative purposes, the studies also included a nanocrystalline Ni coating without embedded graphene oxide flakes. Graphene oxide was characterized by Raman spectroscopy, infrared spectroscopy (FTIR) and transmission (TEM) and scanning (SEM) electron microscopy. Results of studies on the structure of nickel and composite Ni/GO coatings deposited in a bath containing different amount of graphene oxide are presented. The coatings were characterized by scanning electron microscopy, light microscopy, Raman spectroscopy and X-ray diffraction. The adhesion of the prepared coatings to the substrate was examined by the scratch method. The microhardness of the coatings was measured using the Vickers method on perpendicular cross-sections to the surface. Corrosion tests of the coatings were investigated using the potentiodynamic method. The influence of graphene oxide on the structure and properties of composite coatings deposited from baths with different content of graphene oxide was determined.
Nowadays, titanium is one of the most popular materials for aeronautical applications due to its good corrosion resistance, formability and strength. In this paper, rutile reinforced titanium matrix composites were produced via powder metallurgy. The steps included high energy ball milling of raw titanium and rutile powders in a planetary ball mill, which was followed by cold-pressing and sintering without external pressure. For the characterization of the milled powders and the sintered composites, scanning electron microscope, X-ray diffraction and compressive strength examinations were carried out. The results showed that the rutile has a strengthening effect on the titanium matrix. 1 wt% rutile increased the compressive strength compared to the raw titanium. Increasing the milling time of the metal matrix decreased the compressive strength values.
Results of scientific researches show the trend of active using nitrides and borides of transition
metals and their combination in developing protective materials. While single elements
nitrides have been well studied, their multilayer modifications and combinations require
more detailed study. Physical-mechanical properties and structural-phase state of multilayer
coating according to the deposition conditions is an important task for the study.
It will be the analysis of physical-mechanical and electrical properties of coatings based on
refractory metals nitrides, their structure and phase composition and surface morphology
depending on the parameters of condensation. It was established the structure and behavior
of nano scale coatings based on refractory metals nitrides (Ti, Zr) depending on the size
of nano grains, texture, stress occurring in coatings.
Photoactive nanofilled nematic is proposed. Stable three-component photoresponsive nanocomposite was prepared from photo-insensitive nanofilled nematic by inclusion of 3 wt.% azobenzene-containing photoactive mesogen 4-(4′-ethoxyphenylazo)phenyl hexanoate (EPH). The host nanofilled nematic was produced from the room-temperature nematic liquid crystal 4-n-heptyl cyanobiphenyl (7CB) and 3 wt.% filler of Aerosil 300 hydrophilic silica nanospheres of size 7 nm. Apparent effect of stimulation with a relatively weak continuous illumination by UV light (375 nm wavelength) takes place for both the alternating-current electric field-dependent optical transmittance and the electro-optic amplitude-frequency modulation by thin films (25 µm thick) of the EPH/aerosil/7CB nanocomposite. The light-stimulated electro-optics of EPH-doped aerosil/7CB films and the corresponding reversible light control are achieved through trans-cis-trans photoisomerization of the photoactive agent EPH. As such, the initial electro-optical response of the studied photoactive nanocomposites is recovered with continuous blue-light illumination. The examined EPH/aerosil/7CB nanocomposites exhibit photo-controllable electro-optical response that is of practical interest.