The present study, aims to investigate the effect of minor Zr and Nb alloying on soft magnetic and electrical properties of Fe86(ZrxNb1-x)7B6Cu1 (x = 1, 0.75, 0.5, 0.25) alloys. The investigated alloys were prepared through the melt spinning process. Within the examined compositional range (Nb up to 5.25at%, respectively), the soft magnetic properties and electrical resistivity of the alloys continuously increase with increasing Nb content. However increasing the Nb content further decreases such properties. We could confirm the influence of ratio of Zr and Nb on grain growth and crystallization fraction during crystallization by using the soft magnetic properties and electrical properties.
Paper describes the results of Fe80Si11B9 amorphous ribbon investigation after pulsed laser interference heating and conventional annealing. As a result of interference heating periodically placed laser heated microareas were obtained. Structure characterisation by scanning and transmission electron microscopy showed in case of laser heated samples presence of crystalline nanostructure in amorphous matrix. Microscopy observations showed significant difference in material structure after laser heating – nanograin structure, and material after annealing – dendritic structure. Magnetic force microscopy investigation showed expanded magnetic structure in laser heated microareas, while amorphous matrix did not give magnetic signal. Change of magnetic properties was examined by magnetic hysteresis loop measurement, which showed that the laser heating did not have a significant influence on soft magnetic properties.
The AISI 430 stainless steel with ferritic structure is a low cost material for replacing austenitic stainless steel because of its higher yield strength, higher ductility and also better polarisation resistance in harsh environments. The applications of AISI 430 stainless steel are limited due to insignificant ductility and some undesirable changes of magnetic properties of its weld area with different microstructures. In this research, a study has been done to explore the effects of parameters of laser welding process, namely, welding speed, laser lamping current, and pulse duration, on the coercivity of laser welded AISI 430 stainless steel. Vibrating sample magnetometery has been used used to measure the values of magnetic properties. Observation of microstructural changes and also texture analysis were implemented in order to elucidate the change mechanism of magnetic properties in the welded sections. The results indicated that the laser welded samples undergo a considerable change in magnetic properties. These changes were attributed to the significant grain growth which these grains are ideally oriented in the easiest direction of magnetization and also formation of some non-magnetic phases. The main effects of the above-mentioned factors and the interaction effects with other factors were evaluated quantitatively. The analysis considered the effect of lamping current (175-200 A), pulse duration (10-20 ms) and travel speed (2-10 mm/min) on the coercivity of laser welded samples.
In this study, we demonstrate a facile and cost-effective way to synthesize Nd-Fe-B of various shapes such as powders, rods and fibers using electrospinning, heat-treatment and washing procedures. Initially Nd-Fe-B fibers were fabricated using electrospinning. The as-spun Nd-Fe-B fibers had diameters ranging 489 to 630 nm depending on the PVP concentration in reaction solutions. The different morphologies of the Nd2Fe14B magnetic materials were related to the difference in thickness of the as-spun fibers. The relationships between the as-spun fiber thickness, the final morphology, and magnetic properties were briefly elucidated. The intrinsic coercivity of Nd2Fe14B changed with the change in morphology from powder (3908 Oe) to fiber (4622 Oe). This work demonstrates the effect of the Nd-Fe-B magnetic properties with morphology and can be extended to the experimental design of other magnetic materials.