Archives of Metallurgy and Materials | 2018 | vol. 63 | No 3

Download PDF Download RIS Download Bibtex

Abstract

The paper presents the effect of ZrO2 layer deposition by the ALD process on the physicochemical properties of cobalt-based alloys (Realloy C and EOS CoCr SP2) intended for application in prosthetic dentistry. The paper shows the results of the surface roughness measurements made by the AFM method as well as the wettability and free surface energy measurements. Additionally,potentiodynamic tests of pitting corrosion resistance and electrochemical impedance spectroscopy in a solution of artificial saliva were carried out. Tests were carried out on the samples in the initial state and after surface modification with the ZrO2 layer. Based on these results, the usefulness (e.g. enhancement of corrosion resistance and biocompatibility) of the proposed ZrO2 layer on the cobalt alloys was assessed.

Go to article

Authors and Affiliations

A. Ziębowicz
A. Woźniak
B. Ziębowicz
K. Kosiel
G. Chladek
Download PDF Download RIS Download Bibtex

Abstract

The study proposed the model of “guide mark” defects formation on the internal surface of pipes, produced on PRM mills of PRP – 140. The research of pipe forming at plug rolling mill with stub mandrel has been carried out; regularities of the dimensionless parameters characterizing the deformation of the gap release, depending on the reduction ratio, were determined. The model of “guide mark” defect formation on the internal surface of the pipe has been proposed. This allows for lesser wall thickness variation of rough tubes. It has been shown that, when using dioctahedral pass designs in comparison with hexagonal pass designs the proportion of displaced volume along the pipe axis is greater but the value is lower; thereby, the risk of “guide mark” defect forming is reduced.

Go to article

Authors and Affiliations

D. Pavlov
A. Bogatov
E. Pavlova
H. Dyja
Download PDF Download RIS Download Bibtex

Abstract

Weld metal deposit (WMD) was carried out for standard MMA welding process. This welding method is still promising mainly due to the high amount of AF (acicular ferrite) and low amount of MAC (self-tempered martensite, retained austenite, carbide) phases in WMD. That structure corresponds with good impact toughness of welds at low temperature. Separate effect of these elements on the mechanical properties of welds is well known, but the combined effect of these alloy additions has not been analyzed so far. It was decided to check the total influence of nickel with a content between 1% to 3% and molybdenum with content from 0.1% up to 0.5%.

Go to article

Authors and Affiliations

B. Szczucka-Lasota
T. Węgrzyn
A. Kurc-Lisiecka
J. Piwnik
Download PDF Download RIS Download Bibtex

Abstract

In the present paper, the effects of the subsequent extrusion after multi-pass equal-channel angular pressing (ECAP) process on the mechanical properties and microstructure of WE43 magnesium alloy are investigated. First, second and fourth passes ECAP followed by an extrusion process are applied on WE43 magnesium alloy to refine the microstructure and to improve the mechanical properties for biomedical applications. The results showed that among the ECAPed samples, the highest and lowest strength were obtained in the second and the first pass processed samples, respectively. The four passes processed sample showed the highest elongation to failure with moderate strength. The sample processed via first pass ECAP followed by extrusion exhibits an excellent combination of ductility and strength. The highest strength was obtained in the sample processed via the second pass ECAP followed by extrusion while the highest elongation was achieved in the sample processed via fourth pass ECAP followed by extrusion. Moreover, Vickers micro-indentation tests demonstrate that hardness is enhanced by an increase in the number of ECAP passes. Furthermore, a grain refinement process is presented for ECAP processing of WE43 alloy which shows a good agreement with microstructural investigations.

Go to article

Authors and Affiliations

A. Torkian
G. Faraji
M. Karimpour
Download PDF Download RIS Download Bibtex

Abstract

Equal-channel angular pressing (ECAP) was used as a technique for severe plastic deformation (SPD) on Al alloy AA3004. This technique produced fully dense materials of refined grain structure to sub-micrometer dimensions and advanced mechanical properties. The ECAP processing of samples was conducted as 1 to 4 passes through the die at room temperature. We present the results of the studied homogeneity evolution with the ECAP treatment. Furthermore, a Scanning Electron Microscope (SEM) was used for examination of the microstructure changes in samples undergone from 1 to 4 passes. The microhardness-HV increased upon each ECAP pass. The resulting micro-hardness evolution was attributed to crystalline microstructure modifications, such as the d-spacing (studied by X-ray Diffraction-XRD) depending on the number of ECAP pressings. The microcrystalline changes (grain refining evaluated from the Scanning Electron Microscopy – SEM images) were found to be related to the HV, following the Hall-Petch equation.

Go to article

Authors and Affiliations

N. Izairi
F. Ajredini
A. Vevecka-Pfiftaj
P. Makreski
M.M. Ristova
Download PDF Download RIS Download Bibtex

Abstract

The paper presents results of a research on simulation of magnetic tip-surface interaction as a function of the lift height in the magnetic force microscopy. As expected, magnetic signal monotonically decays with increasing lift height, but the question arises, whether or not optimal lift height eventually exists. To estimate such a lift height simple procedure is proposed in the paper based on the minimization of the fractal dimension of the averaged profile of the MFM signal. In this case, the fractal dimension serves as a measure of distortion of a pure tip-surface magnetic coupling by various side effects, e.g. thermal noise and contribution of topographic features. Obtained simulation results apparently agree with experimental data.

Go to article

Authors and Affiliations

M. Bramowicz
S. Kulesza
T. Chrostek
C. Senderowski
Download PDF Download RIS Download Bibtex

Abstract

Aluminum 6082-T6 panels were joined by friction stir welding utilizing a bobbin tool. A thermal simulation of the process was developed based upon machine torque and the temperature dependent yield stress utilizing a slip factor and an assumed coefficient of friction. The torque-based approach was compared to another simulation established on the shear layer methodology (SLM), which does not require the slip factor or coefficient of friction as model inputs. The SLM simulation, however, only models heat generation from the leading edges of the tool. Ultimately, the two approaches yielded matching temperature predictions as both methodologies predicted the same overall total heat generation from the tool. A modified shear layer approach is proposed that adopts the flexibility and convenience of the shear layer method, yet models heat generation from all tool/workpiece interfaces.

Go to article

Authors and Affiliations

C. Hamilton
S. Dymek
A. Węglowska
A. Pietras
Download PDF Download RIS Download Bibtex

Abstract

In this article examinations of hybrid welding technology (laser beam + MAG) of T-joints from thermomechanically worked high strength steel S700MC 10 mm thick were presented. Joints welded from one side and both sides were made. Carried examinations enabled to classify joints in quality level B according to ISO 12932 (Welding. Laser-arc hybrid welding of steels, nickel and nickel alloys. Quality levels for imperfections). In case of one sided welding with partial penetration with beam power of 8.5 kW 8 mm of penetration was achieved without noticeable distortion of web. Double sided joints were characterized with correct geometry. Joint metal is bainitic-ferritic in structure and its hardness rises about 40 HV1 in comparison to base metal hardness (280 HV1). In HAZ a slight softening of material in comparison to base metal is present.

Go to article

Authors and Affiliations

J. Górka
Download PDF Download RIS Download Bibtex

Abstract

In the study, particle size distribution of the MIEX® resin was presented. Such analyses enable to determinate whether presence of fine resin fraction may be the reason for unfavorable membrane blocking during water purification by the hybrid MIEX®DOC – microfiltration/ultrafiltration systems. Granulometric analysis of resin grains using the laser diffraction particle size analyzer (laser granulometer) was carried out as well as the microscopic analysis with scanning electron microscope. The following samples were analyzed: samples of fresh resin (a fresh resin – not used in water treatment processes) and samples of repeatedly used/regenerated resin that were collected to analysis during mixing and after sedimentation process. Particle size distribution was slightly different for fresh resin and for repeatedly used/regenerated resin. The grains sizes of fresh resin reached approximately 60 μm (d10), 120 μm (d50) and 220 μm (d90). Whereas the sizes of repeatedly used/regenerated resin were about 15 μm (d10), 40 μm (d50) and 115-130 μm (d90). The smallest resin grains sizes were in the range of 0.3-0.45 μm. This ensures that the ultrafiltration membranes retain all resin grains, even the smallest ones. Whereas the microfiltration membranes must be appropriately selected to guarantee full separation of the resin grains and at the same time to exclude a membrane pores blocking.

Go to article

Authors and Affiliations

M. Rajca
R.T. Bray
K. Fitobór
K. Gołombek
Download PDF Download RIS Download Bibtex

Abstract

Repeated austenitisation and furnace cooling of homogenised 0.16 wt. % carbon steels result in ferrite grain sizes between 27 μm and 24 μm. Similarly, repeated austenitisation and normal-air cooling produces ferrite grain sizes between 17 μm and 12 μm; while repeated austenitisation and forced-air cooling produces a minimum grain size of 9.5 μm. Furnace cooling decomposes the austenite eutectoidally to lamellar pearlite; while normal-air cooling and forced-air cooling after austenitisation cause degeneration of pearlite regions producing grain boundary network as well as cluster of cementite and other carbides. Forced-air cooled samples provide the highest YS (364 MPa) and UTS (520 MPa); while furnace cooling provides the lowest (290 MPa and 464 MPa) leaving the normal-air cool performance in between. Hardness values depict the role of individual ferrite and pearlite content and the extent of pearlite degeneration occurring after each cyclic treatment.

Go to article

Authors and Affiliations

A.R. Subhani
D.K. Mondal
Download PDF Download RIS Download Bibtex

Abstract

The work reports on the development of random three-dimensional Laguerre-Voronoi computational models for open cell foams. The proposed method can accurately generate foam models having randomly distributed parameter values. A three-dimensional model of ceramic foams having pre-selected cell volumes distribution with stochastic coordinates and orientations was created in the software package ANSYSTM. Different groups of finite element models were then generated using the developed foam modeling procedure. The size sensitivity study shows that each of foam specimens at least contains 125 LV-cells. The developed foam models were used to simulate the macroscopic elastic properties of open cell foams under uni-axial and bi-axial loading and were compared with the existing open cell foam models in the literature. In the high porosity regime, it is found that the elastic properties predicted by random Laguerre-Voronoi foam models are almost the same as those predicted by the perfect Kelvin foam models. In the low porosity regime the results of the present work deviate significantly from those of other models in the literature. The results presented here are generally in better agreement with experimental data than other models. Thus, the Laguerre-Voronoi foam models generated in this work are quite close to real foam topology and yields more accurate results than other open cell foam models.

Go to article

Authors and Affiliations

Z. Nie
Y. Lin
Q. Tong
Download PDF Download RIS Download Bibtex

Abstract

In this research, the high arsenic content dust of copper smelting, as a raw material, the extraction of copper and arsenic from the high arsenic content dust in the leaching system containing acidic and alkaline compounds was investigated. Meanwhile, the effects of acid/alkaline initial concentration, liquid to solid ratio, leaching temperature, leaching time on the leaching rate of copper and arsenic were studied. The optimum conditions for the leaching of high arsenic content dust and preparation of copper arsenate were determined. The results showed that acidic/alkaline leaching of high arsenic content dust was particularly effective. 93.2% of the copper, and 91.6% of the arsenic were leached in an acidic leaching process and 95% of the arsenic, while less than 3% of the copper, less than 5% of the antimony, less than 2% of the bismuth was also leached in an alkaline leaching process. A new method (the parallel flow drop precipitate method) was developed in the synthesis of copper arsenate process. The parallel flow drop method was employed to adjust the molar ratio (copper to arsenic) of the mixed solution of the acid-leaching solution and the alkali-leaching solution by taking the drop acceleration of an acidic leaching solution and an alkaline leaching solution at 10 mL/min and 12 mL/min, at a temperature of 60°C and a reaction time of 1 h. Copper arsenate was prepared by mixing an acidic leaching solution and an alkaline leaching solution. The main phases of copper arsenate were CuHAsO4·1.5H2O and Cu5As4O15·9H2O. Copper arsenate contained 30.13% copper and 31.10% arsenic.

Go to article

Authors and Affiliations

W. Sheng
Y.-Y. Shen
Z. Sheng-Quan
Download PDF Download RIS Download Bibtex

Abstract

The main goal of the presented work was to determine the relationship between changes in the shape of the derivative curve and the microstructure of Zn-Al-Cu alloys before and after modification. To describe the phenomena that occur in the material during solidification as a result of the modification in the chemical composition, the thermal-derivative analysis method was applied. This method allows to describe and interpret the kinetics of crystallisation of the tested alloys. To describe the morphology and phase composition, light and electron microscopy (SEM, TEM) was also used. The modification of the hypereutectic Zn-Al-Cu alloys with the addition of Ce causes a reduction in the size α' + η eutectics and change in the morphology of the α' phase precipitates from dendritic to “tweed”.

Go to article

Authors and Affiliations

M. Krupiński
Download PDF Download RIS Download Bibtex

Abstract

The present investigation has been made to assess the influence of B4C reinforced with Ti-6Al-4V matrix prepared by powder metallurgy route. High energy ball milling was used to prepare the composites. Cylindrical preforms were prepared using suitable die set assembly. The green preforms were sintered in the muffle furnace at 900°C for 1 h. Further the preforms were cooled inside the furnace till the room temperature has attained. SEM with EDS mapping analysis was used to evaluate the morphology and elemental confirmation of the prepared composite. The density and hardness of the samples are determined using Archimedes principle and Rockwell hardness testing machine. The wear resistance of the samples was determined by employing a pin on disc apparatus. The hardness of the composites (Ti-6Al-4V /10B4C) was increased while comparing to the base material (Ti-6Al-4V) which is attributed to the presence of hard ceramic phase. Response Surface Methodology (RSM) five level central composite design approach was accustomed and it minimised the amount of experimental conditions and developed mathematical models among the key process parameters namely wt. % of B4C, applied load and sliding distances to forecast the abrasive response of Specific Wear Rate (SWR) and Coefficient of Friction (CoF). Analysis of variance was used to check the validity of the developed model. The optimum parameters of specific wear rate and coefficient of friction were identified.

Go to article

Authors and Affiliations

T. Ramkumar
P. Narayanasamy
M. Selvakumar
P. Balasundar
Download PDF Download RIS Download Bibtex

Abstract

Hot tearing severity was evaluated in this experiment by introducing a new apparatus called Constrained Rod Casting Modified Horizontal (CRCM-Horizontal). Six constraint bars with different lengths can produce hot tearing on the cast sample. Mold position was modified from vertical to horizontal and the shape was changed from a harp shape to a star shape, which allows for the liquid metal to feed into each rod cavity simultaneously. Hot tearing development was recorded along the bars by a digital camera. A new Hot Tearing Susceptibility (HTS) formula was developed for quantitative investigation of hot tearing on a cast sample. The parameters of the HTS formula are bar length of cast sample (Li), tear severity (Ci) and location of hot tear (Pi). Footprint charts and hot tear scales are used to illustrate hot tearing severity. The experiment was conducted with Al-1.36Zn-1.19Si and Al-5.9Cu-1.9Mg alloys to investigate the sensibility of the apparatus and modification its operation.

Go to article

Authors and Affiliations

V. Malau
Akhyar
P. Tri Iswanto
Download PDF Download RIS Download Bibtex

Abstract

The paper contains the results of the initial surface treatment influence on the properties of the medical Ti-6Al-7Nb alloy with a modified zirconium oxide layer deposited on its surface by sol-gel method. In the paper, the analysis of results of potentiodynamic studies is presented as well as its resistance to pitting corrosion and electrochemical impedance spectroscopy (EIS), macroscopic observation of the surface of samples and analysis of geometrical structure with the use Atomic Force Microscope (AFM) were performed. The studies were performed on two groups of samples depending on the graduation of the sand used in sandblasted process – 50 μm and 250 μm. Based on the obtained results it can be concluded that the type of the initial surface treatment preceding the surface modification of the Ti-6Al-7Nb has a significant effect on its properties.

Go to article

Authors and Affiliations

A. Woźniak
B. Ziębowicz
A. Ziębowicz
W. Walke
Download PDF Download RIS Download Bibtex

Abstract

Ludwigite is the main available boron-bearing resource in China. In order to enrich the theory system and optimize its utilization processes, this paper study the mechanism and kinetics on non-isothermal decomposition of ludwigite in inert atmosphere by means of thermal analysis. Results show that, the decomposition of serpentine and szajbelyite is the main cause of mass loss in the process. At the end of decomposition, hortonolite and ludwigite are the two main phases in the sample. The average E value of structural water decomposition is 277.97 kJ/mol based on FWO method (277.17 kJ/mol based on KAS method). The results is proved to be accurate and reliable. The mechanism model function of structural water decomposition is confirmed by Satava method and Popescu method. The form of the most probable model function is G(α) = (1 – α)–1 – 1 (integral form) and f (α) = (1 – α)2 (differential form), and its mechanism is chemical reaction. This is verified by the criterion based on activation energy of model-free kinetics analysis.

Go to article

Authors and Affiliations

X. Fu
M. Chu
L. Gao
Z. Liu
Download PDF Download RIS Download Bibtex

Abstract

In the present study, Ti6Al4V titanium alloy plates were joined using robotic laser welding method. Pre- and post-weld heat treatments were applied to laser welded joints. After welding stress relieving, solution heat treatment and ageing were also applied to preheated laser welded samples. Effects of heat treatment conditions on microstructural characteristics and mechanical properties of robotic laser welded joints were studied. Aged samples were found to be made of coarsened grains compared to microstructures of non-aged samples. There were increases in ductility and impact toughness of samples applied to ageing increased, while hardness and tensile strength of non-aged samples were higher. The highest value for tensile strength and for impact toughness in welded samples have been identified as 840 MPa and 27 J, respectively. Fractures in tensile test samples and base metal impact test samples took place in the form of ductile fracture, while laser welded impact test samples had fractures in the mode of intergranular fractures with either a quasi-cleavage type or tear ridges. EDS analysis carried out for all heat treatment conditions and welding parameters demonstrated that major element losses were not observed in base metal, HAZ and weld metal.

Go to article

Authors and Affiliations

C. Köse
E. Karaca
Download PDF Download RIS Download Bibtex

Abstract

Group of steel balls with different chemical composition, diameters and nitriding treatment parameters were investigated with using magnetic resonance and magnetization methods. Emerging nitrided regions consists of diffusion and surface layer of iron nitrides. The thickness of the individual layers depends on the type of steel and process parameters. Resonance signal shape and position were successfully described in the ferromagnetic resonance regime expected for dense iron magnetic system. Influence of the sample size, thermal treatment and carbon content on the absorption signal has been analyzed. Significant magnetic anisotropy has been revealed, as well as non-usual increasing of the magnetization as a function of temperature. It suggests, that overall antiferromagnetic ordering, destroyed by thermal movement, lead to increasing of the ferromagnetic region.

Go to article

Authors and Affiliations

H. Fuks
S.M. Kaczmarek
G. Leniec
J. Michalski
B. Kucharska
P. Wach
Download PDF Download RIS Download Bibtex

Abstract

We present the results of investigations of Pb(Fe1/2Nb1/2)O3 (PFN) ceramic samples obtained using two-step synthesis (i.e. columbite method). For obtained samples complex investigations of microstructure, magnetic and electrophysical properties have been performed at low and at high temperatures. Microstructure is characterized by small grains with high homogeneity and high density (low porosity). Impedance of samples and the phase shift angle have been measured using LCR Meter. Next the AC electric conductivity, dielectric permittivity and loss tangent have been calculated. AC conductivity at frequency 3 Hz was measured in similar way using Quantum Design PPMS System in magnetic fields 1000 Oe and 10000 Oe. At temperature range 240K-260K the anomalies of conductivity are observed. These anomalies depend on measuring cycle (heating, cooling) and magnetic field.

Go to article

Authors and Affiliations

D. Bochenek
R. Skulski
P. Niemiec
D. Brzezińska
K. Rogacki
Download PDF Download RIS Download Bibtex

Abstract

The microstructures and mechanical properties of T92 martensitic steel/Super304 austenitic steel weld joints with three welding consumables were investigated. Three types of welding materials ERNiCr-3, ERNiCrCoMo-1and T-304H were utilized to obtain dissimilar welds by using gas tungsten arc weld (GTAW). The results show that heat affect zone (HAZ) of T92 steel consists of coarse-grained and fine-grained tempered martensites. The microstructures of joints produced from ERNiCrCoMo-1 consist of equiaxed dendrite and columnar dendrite grains, which are more complicated than that of ERNiCr-3. In the tensile tests, joints constructed from ERNiCrCoMo-1 and T-304H met the ASME standard. The highest fracture energy was observed in specimens with the welding material ERNiCrCoMo-1. Ni content in weld seam of ERNiCrCoMo-1 was highest, which was above 40%. In conclusion, the nickel alloy ERNiCrCoMo-1 was the most suitable welding material for joints produced from T92 martensitic steel/Super304 austenitic steel.

Go to article

Authors and Affiliations

Z. Liang
Y. Gui
Q. Zhao
Download PDF Download RIS Download Bibtex

Abstract

Studies on biocompatibility of AISI 316LVM steel indicate the need to eliminate the nickel from the surface and replace it with other elements of improved biocompatibility. Therefore, in the presented work selected physicochemical and mechanical properties of the diffusive nitrocarburized layer formed by plasma potential by means of an active screen made of the Fe-Cr-Ni were studied. In the paper we present results of microstructure and phase composition of the layers, roughness, and surface wettability, potentiodynamic pitting corrosion resistance, penetration of ions into the solution as well as mechanical properties. The studies were conducted for the samples of both mechanically polished and nitrocarburized surfaces, after sterilization, and exposure to the Ringer’s solution. Deposition of the nitrocarburized layer increased the contact angle, surface roughness, surface hardness, and corrosion resistance with respect to the polished surfaces. The nitrocarburized layer is a barrier against the ions release into the solution and sterilization and exposure to Ringer solution. The obtained results showed beneficial increase of both mechanical and electrochemical properties of the deposited layer, and thus the applicability of the proposed method of surface treatment of the 316LVM steel for short-term implants after sterylization.

Go to article

Authors and Affiliations

A. Kajzer
K. Rabij
M. Basiaga
K. Nowińska
M. Kaczmarek
T. Borowski
T. Wierzchoń
Download PDF Download RIS Download Bibtex

Abstract

The paper presents the test results for the microstructure of ZnO varistors comprising high voltage gapless surge arresters. The tests were performed on varistors produced in different periods and by various manufacturers. The research was inspired by different characteristics of changes in values of current flowing through surge arresters as a function of changes in values of system voltage in a 220 kV substation, and the temperature in a multi-year cycle. Furthermore, the effects of varistor microstructure degradation following a failure of an unsealed surge arrester were investigated. The results provided the grounds for assessment of ZnO varistor microstructure parameters in terms of their durability and resistance to degradation processes.

Go to article

Authors and Affiliations

P. Papliński
J. Wańkowicz
P. Ranachowski
Z. Ranachowski
Download PDF Download RIS Download Bibtex

Abstract

An optimized method of vibration Energy Harvesting is based on a step-down transformer that regulates the power flow from the piezoelectric element to the desired electronic load. Taking into account parameters of the whole system, the “optimal” voltage gain the piezoelectric transformer can be determined where the harvested power is maximized for the actual level of mechanical excitation. Consequently the piezoelectric transformers can be used to boost up the conversion of mechanical strain into electrical power with considerable potential in Energy Harvesting applications. Nowadays however, the most important factor is usage of lead free material for its construction. Additional desired parameters of such ceramics include high value of piezoelectric coefficients, low dielectric losses and reasonable power density. This work for first time proposes a lead free K0.5Na0.5NbO3 (KNN) material implementation for stack type of piezoelectric transformer that is designed for load efficiency optimization of vibration energy harvester.

Go to article

Authors and Affiliations

L. Kozielski
K. Feliksik
B. Wodecka-Duś
D. Szalbot
S. Tutu
Download PDF Download RIS Download Bibtex

Abstract

This article presents the results of an examination performed on a set of samples of glass-epoxy core rods used in composite insulators with silicone rubber housings. The goal of the examination was to test the aging resistance of the core material when exposed to Direct Current (DC) high voltage. Long term exposure of a glass-epoxy core rod to DC high voltage may lead to the gradual degradation of its mechanical properties due to the ion migrations. Electrolysis of the core material (glass fiber) may cause electrical breakdown of the insulators and consequently lead to a major failure. After being aged for 6000 hours under DC high voltage, the samples were subjected to microscopic analysis. Their chemical composition was also examined using Raman spectroscopy and their dielectric losses and conductance in the broad range of frequencies were tested using dielectric spectroscopy.

Go to article

Authors and Affiliations

K. Wieczorek
M. Jaroszewski
P. Ranachowski
Z. Ranachowski
Download PDF Download RIS Download Bibtex

Abstract

The purpose of this paper was to search the relations between the structure of the compressed expanded graphite – polymer – turbostratic carbon composites on successive stages of technological treatment and parameters describing the acoustic emission phenomena in these materials. The acoustic emission method can be used for measurements of changes in the structure and many different properties of materials. These investigations are a continuation of our earlier studies concerning physical, mechanical and chemical properties of porous composites created on the basis of a compressed expanded graphite matrix, obtained after successive technological procedures of impregnation, polymerization and carbonization of polyfurfuryl alcohol. The aim of this work was to investigate materials obtained at different levels of technological processing, thus with different densities, porosity, physical and chemical properties, by using the acoustic emission method. In compressed expanded graphite composites structures one can differentiate two basic directions: perpendicular to the bedding plane of graphite flakes and parallel to this one. The all presented results were obtained for the uniaxial strain applied in the direction perpendicular to the bedding plane of the composite structure. Analysis of acoustic emission parameters provides information on physical and chemical processes in these materials.

Go to article

Authors and Affiliations

A. Berdowska
J. Berdowski
F. Aubry
Download PDF Download RIS Download Bibtex

Abstract

The discovery of (BaxCa1-x)(ZryTi1-x)O3 lead-free ceramics drawn a lot of attention to those novel materials because of their excellent piezoelectric properties. However, quite a little attention has been paid to other features of the material. This article reports a wide range of research, including composition, structure and microstructure, dielectric response and impedance spectroscopy in order to systematize and expand knowledge about this peculiar ceramics and strontium doping effect on its properties. In order to test that influence a series of samples with various strontium concentration, precisely the admixtures of 0.02, 0.04 and 0.06 mol% were prepared, as well as basic ceramics to compare obtained results.

Go to article

Authors and Affiliations

D. Radoszewska
T. Goryczka
M. Adamczyk
B. Wodecka-Duś
D. Bochenek
L. Kozielski
Download PDF Download RIS Download Bibtex

Abstract

The wear behaviour of Cr3C2-25% NiCr laser alloyed nodular cast iron sample were analyzed using a pin-on-disc tribometer. The influence of sliding velocity, temperature and load on laser alloyed sample was focused and the microscopic images were used for metallurgical examination of the worn-out sites. Box-Behnken method was utilised to generate the mathematical model for the condition parameters. The Response Surface Methodology (RSM) based models are varied to analyse the process parameters interaction effects. Analysis of variance was used to analyse the developed model and the results showed that the laser alloyed sample leads to a minimum wear rate (0.6079×10–3 to 1.8570×10–3 mm3/m) and coefficient of friction (CoF) (0.43 to 0.53). From the test results, it was observed that the experimental results correlated well with the predicted results of the developed mathematical model.

Go to article

Authors and Affiliations

N. Jeyaprakash
M. Duraiselvam
R. Raju
Download PDF Download RIS Download Bibtex

Abstract

The contributions of work-hardening of austenite and the presence of martensite on the hardening of an AISI 304L stainless steel were evaluated based on plastic deformation under different reductions in thickness at two rolling temperatures. The cold deformation temperatures of 300 K and 373 K were chosen to induce strain-hardening plus strain-induced martensitic transformation in the former and strain-hardening in the latter. This made it possible to elucidate the real effects of strengthening mechanisms of metastable austenitic stainless steels during mechanical working.

Go to article

Authors and Affiliations

T. Mirzaie
H. Mirzadeh
M. Naghizadeh
Download PDF Download RIS Download Bibtex

Abstract

This paper is focused on the manufacturing and properties of light weight aggregates made from local waste materials. The waste materials were car windshield glass contaminated by PVB foil, fly ash, mine slates as well as wastes after toothpaste production. The main aim of the research was to combine car windshield glass and the aluminosilicate coal mine slates as a basis for light weight aggregates manufacturing. Fly ash were added in order to modify rheological properties of the plastic mass. Toothpaste wastes were introduced as a source of carbonates and CO2 evolution during thermal treatment. After milling and mixing all materials they were pressed and sintered at temperature range of 950°C-1100°C in air. The results show that it is possible to receive light weight aggregates only from the Silesian local waste materials. The significant influence of sintering temperature on properties of aggregates was observed.

Go to article

Authors and Affiliations

J. Smoleń
T. Pawlik
M. Sopicka-Lizer
D. Michalik
Download PDF Download RIS Download Bibtex

Abstract

The casting workshop was discovered with numerous artifacts, confirming the existence of the manufacturing process of metal ornaments using ceramic molds and investment casting technology in Lower Silesia (Poland) in 7-6 BC. The research has yielded significant technological information about the bronze casting field, especially the alloys that were used and the artifacts that were made from them. Based on the analyses, the model alloys were experimentally reconstructed. Taking advantage of the computer-modeling method, a geometric visualization of the bronze bracelets was performed; subsequently, we simulated pouring liquid metal in the ceramic molds and observed the alloy solidification. These steps made it possible to better understand the casting processes from the perspective of the mold technology as well as the melting and casting of alloys.

Go to article

Authors and Affiliations

A. Garbacz-Klempka
J.S. Suchy
Z. Kwak
P. Długosz
T. Stolarczyk
Download PDF Download RIS Download Bibtex

Abstract

This work reports the results of a study of Mo thin films synthesis by DC Pulsed Magnetron Sputtering method (PMS), operating at pulse main frequency of 100 kHz and modulated by the additional modulation frequency, driving in the range of 5-1000 Hz (modulated Pulse Magnetron Sputtering – mPMS). We have studied the influence of mPMS on plasma chemical reactions and mechanisms of layer growth using optical emission spectroscopy technique. Our experiment showed strong influence of mPMS method, on the morphology (scanning electron microscopy), phase composition (X-ray diffractometry) and electric properties (4-point probes method) of nanocrystalline and amorphous Mo films. From the utilitarian point of view, low value of resistivity – 43,2 μΩcm of synthesized Mo films predestines them as back contacts for thin solar cells CIGS. Our results revealed that additional modulation frequency should be considered as an important factor for optimization of films synthesis by means of PMS-based methods.

Go to article

Authors and Affiliations

B. Wicher
R. Chodun
K. Nowakowska-Langier
S. Okrasa
K. Król
R. Minikayev
G. Strzelecki
K. Zdunek
Download PDF Download RIS Download Bibtex

Abstract

This paper presents the findings of fatigue strength tests of 15CrNi6 steel following low-pressure carburizing and oil quenching, subjected to cycles of one-sided three-point bending. The fatigue fractures were compared with the results of fatigue strength studies of 16MnCr5 steel following low-pressure carburizing and nitrogen quenching. The fatigue tests for 16MnCr5 steel were conducted as part of a high-cycle resonance test, with a pendular bending load. The study also involved an analysis of the effects on non-metallic inclusions in the structure on the mechanism of fatigue destruction. The inclusions were found to initiate fatigue cracks. In both cases, a similar method of a fatigue fissure initiation was observed, independent of the study method or specimen material.

Go to article

Authors and Affiliations

S. Lipa
J. Sawicki
K. Dybowski
R. Pietrasik
B. Januszewicz
Download PDF Download RIS Download Bibtex

Abstract

The aim of this research was to fabricate and study the properties of Bi1-x DyxFeO3 (for x = 0, 0.05, 0.07, 0.1) ceramics materials. Simple oxide powders Bi2O3, Dy2O3 and Fe2O3 were used to fabricate Bi1-xDyxFeO3 ceramics by mixed oxide method followed by free sintering. The study presents changes in microstructure and crystal structure as well as in dielectric properties and magnetic properties caused by modification of BiFeO3 with dysprosium dopant.

Go to article

Authors and Affiliations

J. Dzik
K. Feliksik
T. Pikula
R. Panek
M. Rerak
Download PDF Download RIS Download Bibtex

Abstract

The aim of this work was to investigate the possibility of obtaining an amorphous/crystalline composite starting from Ni-Si- B-based powder grade 1559-40 and silver powder. The alloy was produced using arc melting of 95% wt. Ni-Si-B-based powder (1559-40) and 5% wt. Ag powder. Ingot was re-melted on a copper plate and observed while cooling using a mid-wave infra-red camera. The alloy was then melt-spun in a helium atmosphere. The microstructure of the ingot as well as the melt-spun ribbon was studied using light microscopy and scanning electron microscopy with energy dispersive spectrometry. Phase identification was performed by means of X-ray diffraction. The observations confirmed an amorphous/crystalline microstructure of the ribbon where the predominant constituent of the microstructure was an amorphous phase enriched with Ni, Si, and B, while the minor constituent was an Ag-rich crystalline phase distributed in a film along the melt-spinning direction.

Go to article

Authors and Affiliations

M. Wojciechowska
K. Ziewiec
D. Mucha
Download PDF Download RIS Download Bibtex

Abstract

The aim of the study was to evaluate the influence of different fillers on the chosen functional properties of experimental composites based on typical polymeric matrix, in order to understand the effect of different fillers on their properties and to develop a simple base composite for further investigations with experimental fillers, e.g. with antimicrobial properties. Previous experiments have been usually based on commercially available composites of unknown composition or compilation of monomers, without reinforcing fillers. Scanning electron microscopy was used to investigate the quality of fillers’ dispersion, which was satisfying. Results showed significant differences between materials’ diametral tensile strength (p = 0.0019), compressive strength (p < 0.0001), Vickers micro-hardness (p < 0.0001), flexural modules (p = 0.0018), and the degree of conversion (p < 0.0001), but flexural strength was not significantly different (p = 0.0583). Investigations indicated that no filler type had an especially positive impact on the mechanical properties, but reinforcement effect was achieved by proper compilation of silica nanofiller and variable glass fillers. Nanofiller decreased the degree of conversion.

Go to article

Authors and Affiliations

R. Stencel
W. Pakieła
I. Barszczewska-Rybarek
J. Żmudzki
J. Kasperski
G. Chladek
Download PDF Download RIS Download Bibtex

Abstract

The paper analyses the influence of chemical composition of silicone-based composites on their properties in the aspect of using them as long-term soft denture lining materials. Different concentrations of filler and methylhydrosiloxane-dimethylsiloxane copolymer were used. The filler was introduced into the composite with mechanical mixing combined with ultrasonic homogenization. Scanning electron microscopy was used to investigate the quality of filler dispersion. Shore A hardness, tensile strength, sorption, solubility and tensile bond strength to poly(methyl methacrylate) were measured. Tests show satisfactory results for some experimental composites, which met all the requirements for such materials.

Go to article

Authors and Affiliations

E. Jabłońska-Stencel
W. Pakieła
J. Żmudzki
J. Kasperski
G. Chladek
Download PDF Download RIS Download Bibtex

Abstract

The article presents the results of studies on the efficacy of water desalination (i.e. Elimination of NaCl ions from the solution) using graphene-polyamide composite membranes. The membrane used for filtration consists of a monolayer of polycrystalline graphene on a porous polyamide carrier support (nylon 66). The degree of desalination for an aqueous NaCl solution percolated through the membrane was 18%. In the future this type of membrane may replace the currently used reverse osmosis membranes.

Go to article

Authors and Affiliations

K. Dybowski
P. Kowalczyk
P. Kula
A. Jeziorna
R. Atraszkiewicz
Ł. Kołodziejczyk
P. Zawadzki
D. Nowak
T. Kazimierczak
M. Kucińska
Download PDF Download RIS Download Bibtex

Abstract

Twist extrusion is a processing method involving the extrusion of a sample with a prismatic cross-section using a tool composed of four prismatic parts bisected by a screw component. A beneficial change in mechanical durability is one of the main factors enabling the use of highly durable Al-Mg-Mn-Sc-Zr alloys to construct functional components of non-stationary robots. As part of the present research, ANSYS® software was used to simulate a twist extrusion process. An analysis of a sample entering and passing through the entire twisting area was performed, up to the point of full twisting of the base of the sample. The stress conditions in the sample were analysed as it passed through the twisting area. The highest stress values (reaching up to 600 MPa) were detected at the tips of the sample face as the sample exited the twisting area. The lowest stress values, at around 170 MPa, were detected at the side edges of the sample.

Go to article

Authors and Affiliations

J. Sawicki
J. Świniarski
M. Stegliński
P. Byczkowska
Download PDF Download RIS Download Bibtex

Abstract

In ceramic forming techniques high particles packing can provide better properties of the final ceramic products. The high quality of the material coupled with the shape complexity of the ceramic product is still challenging. The aim of this work was the optimization and preparation of the ceramic samples based on two alumina powders of different particle size (AA05: 0.5 μm and TM-DAR: 0.15 μm). Firstly, ceramic suspensions of 50vol.% solid loading and the volumetric ratio of AA05 to TM-DAR 1:1, 2:1, 3:1, 4:1, respectively have been prepared. The 2-carboxyethyl acrylate was applied as the new monomer limiting the negative effect of oxygen inhibition. Additionally, the cold isostatic pressing (CIP) was used in order to increase relative density of green bodies. The results of presented research have shown that samples with the ratio of AA05 to TM-DAR 2:1 were characterized by the highest green density (62%). Moreover, CIP process proved to be effective and increased the density of green bodies from 62% to 67%. The pore size distribution of the green bodies has been measured. Samples were sintered at different conditions (1400°C, 1450°C and 1500°C for 1h and 1300°C, 1400°C, 1450°C and 1500°C for 5h).

Go to article

Authors and Affiliations

P. Wiecińska
E. Pietrzak
Y. Sakka
J. Nakamura
M. Szafran
Download PDF Download RIS Download Bibtex

Abstract

In the work five ceramic compounds based on the (K0.44Na0.52Li0.04)NbO3 (KNLN) material modified with oxides: Cr2O3, ZnO, Sb2O3 or Fe2O3 (in an amount of 0.5 mol.%) were obtained. The KNLN-type composition powder was prepared by solid phase synthesis from a mixture of simple oxides and carbonates, while compacted of the ceramic samples was conducted by free sintering methods. In the work the effect of the used admixture on the electrophysical properties of the KNLN ceramics was presented. The XRD, EDS tests, the SEM measurements of the morphology ceramic samples, dielectric properties and DC electric conductivity were conducted. The research showed that the used admixtures introduced into the base of KNLN-type composition improve the microstructure of the ceramic samples and improve their sinterability. In the case of the dielectric measurements, it was observed a decrease in the maximum dielectric permittivity at the TC for dopred KNLN-type samples. The addition of an admixture of chromium, zinc, antimony or iron in an amount of 0.5 mol.% to the base composition (K0.44Na0.52Li0.04)NbO3 practically does not change the phase transition temperature. The diminution in the density value of doped KNLN ceramics was attributed to the alkali elements volatilization.

Go to article

Authors and Affiliations

D. Bochenek
K. Osińska
P. Niemiec
M. Adamczyk
T. Goryczka
R. Szych
Download PDF Download RIS Download Bibtex

Abstract

In this study, high performance magnesium-yttria nanocomposite’s room temperature, strength and ductility were significantly enhanced by the dispersion of nano-sized nickel particles using powder blending and a microwave sintering process. The strengthening effect of the dispersed nano-sized nickel particles was consistent up to 100°C and then it gradually diminished with further increases in the test temperature. The ductility of the magnesium-yttria nanocomposite remained unaffected by the dispersed nano-sized nickel particles up to 100°C. Impressively, it was enhanced at 150°C and above, leading to the possibility of the near net shape fabrication of the nanocomposite at a significantly low temperature.

Go to article

Authors and Affiliations

Fida S. Hassan
Khin Sandar Tun
F. Patel
Nasser Al-Aqeeli
M. Gupta
Download PDF Download RIS Download Bibtex

Abstract

In the case of mining machines, tribocorrosion damage is often observed. This type of consumption is caused by the joint action of mining environment factors such as abrasive and water. The search for methods to counteract tribocorrosion is of great practical importance, but it must be combined with the knowledge of methods of forecasting the value of wear. This paper presents a model of prediction of tribocorrosive wear adapted to corrodible materials – ADI containing Ni and Cu, with the strength class of 800 MPa – and results of a two-stage study on the tribocorrosive wear. Presented results indicate a distinct effect of synergy between friction and corrosion in the total wear of ADI. The tribocorrosion tests confimed the adequacy of the model developed for the ADI.

Go to article

Authors and Affiliations

A.N. Wieczorek
A. Stachowiak
W. Zwierzycki
Download PDF Download RIS Download Bibtex

Abstract

Operating conditions turbocharger (high temperature and corrosive environment) mean that the device is classified into one of the most elements of the emergency drive unit of the car. The failure rate can be reduced through the use of modern heat-resistant materials, which include based alloys FeAl intermetallic phase. Intermetallic alloys belong to the group of materials known as prospective due to their advantageous properties, in particular their high specific strength, high melting point and good resistance to corrosion and oxidation at high temperatures. In the article presented results of the research axis roll control system variable geometry blades made of intermetallic alloy Fe40Al5Cr0,2TiB as a substitute so far made of austenitic steel. A verification service conditions, comparing the degradation of the material previously used by manufacturers of turbochargers for elements of the control system degradation axes made of intermetallic alloy Fe40Al5Cr0,2TiB. The study consisted of determining microstructure and corrosion products after use. Observations of the structure and the surface of the corrosion tests were performed using light microscopy, scanning electron microscopy and X-ray microanalysis EDS chemical composition.

Go to article

Authors and Affiliations

J. Cebulski
D. Pasek
Download PDF Download RIS Download Bibtex

Abstract

The β-phase Titanium (β-Ti) alloys have been under the spotlight in the recent past for their use as biomedical prosthetic materials owing to their excellent properties such as low elastic modulus, high corrosion resistance and tensile strength. Recently, Niobium (Nb) has gained a lot of attention as a β-phase stabilizing element in Ti alloys to replace Vanadium (V) due to its excellent solubility in Ti, low elastic modulus and biocompatibility. In this work, low cost Ti-20Nb binary alloy has been fabricated via powder metallurgy procedures. The blended powder mixtures of Ti and Nb were sintered at 900°C for 20 mins by the Spark Plasma Sintering (SPS) with an applied uniaxial pressure of 40 MPa. The heating rate was fixed at 50°C/min. The sintered alloy was subject to heat treatments at 1200°C in vacuum condition for various time durations. The characterizations of microstructure obtained during this process were done using FE-SEM, EDS and XRD. By increasing heat treatment time, as understood, the volume of residual Nb particles was decreased resulting in accelerated diffusion of Nb into Ti. Micro hardness of the alloy increased from 340 to 355 HV with the increase in β phase content from 30 to 45%. The resultant alloys had relatively high densities and homogenized microstructures of dispersed lamellar β grains in α matrix.

Go to article

Authors and Affiliations

M.A. Haq
S.F. Abbas
Nu Si A. Eom
T.S. Kim
B. Lee
K.-T. Park
B.S. Kim
Download PDF Download RIS Download Bibtex

Abstract

Neodymium-Iron-Boron (Nd-Fe-B) magnets are considered to have the highest energy density, and their applications include electric motors, generators, hard disc drives, and MRI. It is well known that a fiber structure with a high aspect ratio and the large specific surface area has the potential to overcome the limitations, such as inhomogeneous structures and the difficulty in alignment of easy axis, associated with such magnets obtained by conventional methods. In this work, a suitable heat-treatment procedure based on single-step and multistep treatments to synthesize sound electrospun Nd-Fe-B-O nanofibers of Φ572 nm was investigated. The single-step heat-treated (directly heat-treated at 800°C for 2 h in air) samples disintegrated along with the residual organic compounds, whereas the multistep heat-treated (sequential three-step heat-treated including three steps;: dehydration (250°C for 30 min in an inert atmosphere), debinding (650°C for 30 min in air), and calcination (800°C for 1 h in air)) fibers maintained sound fibrous morphology without any organic impurities. They could maintain such fibrous morphologies during the dehydration and debinding steps because of the relatively low internal pressures of water vapor and polymer, respectively. In addition, the NdFeO3 alloying phase was dominant in the multistep heat-treated fibers due to the removal of barriers to mass transfer in the interparticles.

Go to article

Authors and Affiliations

Eun Ju Jeon
Nu Si A. Eom
Jimin Lee
Bin Lee
Hye Mi Cho
Ji Sun On
Yong-Ho Choa
Bum Sung Kim
Download PDF Download RIS Download Bibtex

Abstract

A nanocrystalline Ti alloy powder was fabricated using cryomilling. The grain size and lattice strain evolution during cryomilling were quantitatively analyzed using X-ray diffraction (XRD) based on the Scherrer equation, Williamson-Hall (W-H) plotting method, and size-strain (S-S) method assuming uniform deformation. Other physical parameters including stress and strain have been calculated. The average crystallite size and the lattice strain evaluated from XRD analysis are in good agreement with the result of transmission electron microscopy (TEM).

Go to article

Authors and Affiliations

M. Oh
H.K. Yu
J.-H. Lee
M.C. Oh
S.-H. Jung
B. Ahn
Download PDF Download RIS Download Bibtex

Abstract

A nanocrystalline Ti alloy powder was fabricated using cryomilling. The grain size and lattice strain evolution during cryomilling were quantitatively analyzed using X-ray diffraction (XRD) based on the Scherrer equation, Williamson-Hall (W-H) plotting method, and size-strain (S-S) method assuming uniform deformation. Other physical parameters including stress and strain have been calculated. The average crystallite size and the lattice strain evaluated from XRD analysis are in good agreement with the result of transmission electron microscopy (TEM).

Go to article

Authors and Affiliations

I.-J. Park
D.-W. Kim
G.-H. Kim
H.-J. Chae
S.-H. Jung
Download PDF Download RIS Download Bibtex

Abstract

U-type ferrite typified by Ba4Co2Fe36O60 is used as a RAM (Radar Absorbing Materials) in the X-band (8-12 GHz). Ba4Co2Fe36O60 is known to have a complex crystal structure, which makes it difficult to obtain single phase and have low reproducibility. Previously known U-type ferrites have been fabricated based on a ceramic process that mixing (by a ball mill), calcining, grinding, binder mixing, drying, sieving, pressing and sintering. In contrast, the process of preparing the powder by the sol-gel method and its heat-treating is advantageous in that it can reduce the process steps and the required time. In addition, the precise stoichiometric control by the sol-gel method can effectively evaluate the effect of added or substituted elements. In this study investigates the crystal structure of Ba4Co2Fe36O60 synthesized by the sol-gel method and the morphology of U-type ferrite nano-powders according to various heat treatment conditions. Analysis of the crystal structure is used for XRD. Morphology and size are observed by SEM. In addition, VSM is performed to confirm the change of magnetic properties according to various heat treatment conditions.

Go to article

Authors and Affiliations

K.-P. Jeong
S.-W. Yang
J.-G. Kim
Download PDF Download RIS Download Bibtex

Abstract

In this study, copper nanoparticles and nanofluids were synthesized by electrical explosion of wire (EEW) in liquid media such as water, ethanol, and acetone. The effect of the different conditions on the properties of the as-synthesized Cu powders and nanofluids were investigated. X-ray diffraction (XRD) analysis was employed to measure the phase of the as-synthesized powder. Only pure Cu phase appeared in case of acetone condition, but CuO and CuO2 phases could be observed in the others. The EEWed particle size was broadened from under 50 to 100 nm. The results showed that acetone was the best condition for achieving smaller particles, preventing the oxidation of the Cu particles and good stability of the nanofluids.

Go to article

Authors and Affiliations

M.-T. Nguyen
J.-H. Kim
J.-C. Kim
Download PDF Download RIS Download Bibtex

Abstract

Fe-Cr-B alloy is a material with precipitation of boride inside Fe matrix, and it features outstanding hardness and wear resistance properties. However, Fe-Cr-B alloy is a difficult material to process, making it difficult to use as a bulk type structure material which requires delicate shapes. This study attempted to manufacture Fe-Cr-B alloy using a 3D printing process, laser metal deposition. This study also investigated the microstructure, hardness and compression properties of the manufactured alloy. Phase analysis results is confirmed that α-Fe phase as matrix and (Cr, Fe)2B phase as reinforcement phase. In the case of (Cr, Fe)2B phase, differences were observed according to the sample location. While long, coarse, unidirectional needle-type boride phases (~11 μm thickness) were observed in the center area of the sample, relatively finer boride phases (~6 μm thickness) in random directions were observed in other areas. At room temperature compression test results confirmed that the sample had a compression strength is approximately 2.1 GPa, proving that the sample is a material with extremely high strength. Observation of the compression fracture surface identified intergranular fractures in areas with needle-type boride, and transgranular fractures in areas with random borides. Based on this results, this study also reviewed the deformation behavior of LMD Fe-Cr-B alloy in relation to its microstructures.

Go to article

Authors and Affiliations

Y.-A. Joo
T.-S. Yoon
S.-H. Park
K.-A. Lee
Download PDF Download RIS Download Bibtex

Abstract

This study attempted to manufacture an Y2O3 ceramic coating layer on a ceramic (AlN) substrate using aerosol deposition (AD) and investigated its macroscopic properties. Pure Y2O3 powder with a polygonal shape and average size of 5.0 μm was used as initial feedstock. Using aerosol deposition with suitable process conditions, an Y2O3 coating layer was successfully fabricated on aluminum nitride (AIN). The thickness of the manufactured coating layer was approximately 10 mm. The coating layer consisted of Y2O3 phase identical to that in the initial powder, and no additional oxides were identified. In regard to the roughness of the Y2O3 coating layer, the average roughness (Ra) measured 1.32 μm, indicating that the surface roughness was relatively even compared to the initial powder size (5 μm). Mechanical properties of the Y2O3 coating layer were measured using nano indentation equipment, and the indentation modulus of the Y2O3 coating layer fabricated by aerosol deposition measured 136.5 GPa. The interface of the coating layer was observed using TEM, and the deposition mechanism of the Y2O3 coating layer manufactured by aerosol deposition was also discussed.

Go to article

Authors and Affiliations

D.-Y. Wi
G.-S. Ham
S.-H. Kim
K.-A. Lee
Download PDF Download RIS Download Bibtex

Abstract

The objective of the present study was to investigate the effects of Sn addition on the mechanical and corrosion properties of Mg-1Zn-1Zr-xSn (x = 1, 2, 3, 4, 5 wt.%) alloys prepared by powder-in-tube rolling (PTR) method. The PTR-treated Mg alloys reached 98.3% of theoretical density. The hardness of the alloy increased with Sn addition. Two main intermetallic phases, Mg2Sn and Zn2Zr3, were formed in the alloys. The Mg2Sn intermetallic particles were observed along the grain boundaries, while the Zn2Zr3 particles were distributed in the Mg matrix. The addition of 1 wt. % Sn caused the corrosion potential to shift toward a more positive value, and the resulting alloy exhibited low corrosion current density.

Go to article

Authors and Affiliations

A. Zakiyuddin
K. Lee
Download PDF Download RIS Download Bibtex

Abstract

Nano-sized yttria (Y2O3) powders were synthesized by a polymer solution route using polyvinyl alcohol (PVA) as an organic carrier. The PVA polymer affected the dispersion of yttrium ions in precursor sol. In this study, three kinds of PVA polymer (different molecular weight) were applied for synthesis of yttria powder. The PVA type as well as calcination temperature had a strongly influence on the particle morphology. Single crystal nano wire particles were observed at the temperature of polymer burn out range and the size was dependent on the PVA type. The stable, fully crystallized yttria powder was obtained through the calcination at 800°C for 1 h. The yttria powder prepared with the high weight PVA (MW: 153,000) revealed a particle size of 30 nm with a surface area of 18.8 m2/g.

Go to article

Authors and Affiliations

Y.-K. Yang
S.-J. Lee
Download PDF Download RIS Download Bibtex

Abstract

The mechanical behavior and the change of retained austenite of nanocrystalline Fe-Ni alloy have been investigated by considering the effect of various Ni addition amount. The nanocrystalline Fe-Ni alloy samples were rapidly fabricated by spark plasma sintering (SPS). The SPS is a well-known effective sintering process with an extremely short densification time not only to reach a theoretical density value but also to prevent a grain growth, which could result in a nanocrystalline structures. The effect of Ni addition on the compressive stress-strain behavior was analyzed. The variation of the volume fraction of retained austenite due to deformation was quantitatively measured by means of x-ray diffraction and microscope analyses. The strain-induced martensite transformation was observed in Fe-Ni alloy. The different amount of Ni influenced the rate of the strain-induced martensite transformation kinetics and resulted in the change of the work hardening during the compressive deformation.

Go to article

Authors and Affiliations

D. Park
S.-J. Oh
I.-J. Shon
S.-J. Lee
Download PDF Download RIS Download Bibtex

Abstract

Y2O3-MgO nanocomposites are one of the most promising materials for hypersonic infrared windows and domes due to their excellent optical transmittance and mechanical properties. In this study, influence of the calcination temperature of Y2O3-MgO nanopowders on the microstructure, IR transmittance, and hardness of Y2O3-MgO nanocomposites was investigated. It was found that the calcination temperature is related to the presence of residual intergranular pores and grain size after spark plasma sintering. The nanopowders calcined at 1000°C exhibits the highest infrared transmittance (82.3% at 5.3 μm) and hardness (9.99 GPa). These findings indicated that initial particle size and distribution of the nanopowders are important factors determining the optical and mechanical performances of Y2O3-MgO nanocomposites.

Go to article

Authors and Affiliations

S.-M. Yong
D.H. Choi
K. Lee
S.-Y. Ko
D.-I. Cheong
Download PDF Download RIS Download Bibtex

Abstract

The effect of additives on the densification behavior and mechanical properties of pure and additive (Zr, B and Mg)-added silica ceramics were investigated for their application to the matrix phase of a silica fiber reinforced silica (SiO2/SiO2f) composite. The additives affected the rate of densification and crystallization (or transformation) of the amorphous silica. Among the compositions, pure silica ceramics sintered at 900°C for 1 h showed the maximum flexural strength. Based on the results, SiO2/SiO2f was fabricated by a repeated vacuum-assisted infiltration method followed by the heat treatment at 900°C for 1 h. The relative density of the composite was 78.2% with a flexural strength of 22.4 MPa. Fractography revealed that the composite was damaged by strong bonding at the fiber/matrix interface and the fracture of fiber.

Go to article

Authors and Affiliations

S.-Y. Ko
S.-M. Yong
S.J. Lee
D.-I. Cheong
S. Baek
Download PDF Download RIS Download Bibtex

Abstract

A cold roll-bonding process was applied to fabricate an AA1050/AA6061/AA1050 multi-layer sheet. Three Al sheets in which an AA6061 sheet is inserted inside two AA1050 sheets of 2 mm thickness, 40 mm width and 300 mm length were stacked up after surface treatment, and the material was then reduced to a thickness of 1.0 mm by multi-pass cold rolling. The AA1050/AA6061/ AA1050 laminate complex sheet fabricated by roll bonding was then hardened by a natural aging (T4) and an artificial aging (T6) treatments. The microstructures of the as-roll bonded and the age-hardened Al complex sheets were revealed by optical microscope and electron back scatter diffraction analysis, and the mechanical properties were investigated by tensile and hardness testing. The strength of the as-roll bonded complex sheet was found to increase by 2.6 times, compared to that value of the starting material. Both AA1050 and AA6061 showed a typical recrystallization structure in which the grains were equiaxed after heat treatment. However, the grain size was smaller in AA6061 than in AA1050.

Go to article

Authors and Affiliations

S.-H. Lee
Download PDF Download RIS Download Bibtex

Abstract

In this study, the combined effect of Zr and Si on isothermal oxidation of Ti for 25 and 50 h at 820°C, which is the temperature related to exhaust valves operation, was investigated. Si addition into Ti-5mass%Zr alloy led to a distribution of silicide Ti5Si3 phase formed by a eutectic reaction. The Ti sample containing only Zr showed more retarded oxidation rate than Ti-6Al-4V, the most prevalent Ti alloy, at the same condition. However, while a simultaneous addition of Zr and Si resulted in greater increase of oxidation resistance. The oxide layer formed after the addition of Zr and Si comprised TiO2, ZrO2, and SiO2.

Go to article

Authors and Affiliations

S.-H. Ha
B.-H. Kim
Y.-O. Yoon
H.-K. Lim
S.K. Kim
Download PDF Download RIS Download Bibtex

Abstract

Macroporous silica fibers having spherical cavities were fabricated by electrospinning using the spinning solution prepared from the mixed dispersion of tetraethylorthosilicate (TEOS) and polystyrene nanospheres as precursor and sacrificial templates, respectively, by injection through metallic nozzle. By applying electric field, the electro-spun fibers obtained by evaporation-driven self-assembly were collected on flat substrate or rotating drum, followed by the removal of the templates by calcination. The sound absorption coefficient of the porous fibers was measured by impedance tube, and the measured value was larger than 0.9 at high frequency region of incident waves. The surface of the resulting fibers was modified using fluorine-containing silane coupling agent to produce superhydrophobic fibrous materials to prevent the infiltration of humidity.

Go to article

Authors and Affiliations

Y.-S. Cho
H. Jin Lee
Download PDF Download RIS Download Bibtex

Abstract

In this study, variations in the contact resistance of electroplated Au-Fe alloy layers with Fe content were investigated. The contact resistance of electroplated Au-Fe alloy layers that were subject to thermal aging at 260°C in the atmosphere, tended to increase significantly with an increase in the Fe content. Through an analysis method employing X-ray photoelectron spectroscopy (XPS/ ESCA) and Auger electron spectroscopy (AES), Ni oxides, such as NiO and Ni2O3, on the surface of the thermally aged electroplated Au-Fe alloy layers were observed. It is believed that the Ni oxide existing on the surface diffused from the underlying electroplated Ni layers to the surface through the grain boundaries in the electroplated Au-Fe layers during the thermal aging. As the Fe content in the electroplated Au-Fe layers increased, the grain size decreased. As the grain size decreases, more Ni oxide was detected on the surface. Therefore, with a rise in the Fe content, more Ni diffuses to the surface via grain boundaries, and more Ni oxide is formed on the surface of the electroplated Au-Fe layers, increasing the contact resistance of the electroplated Au-Fe alloy layers.

Go to article

Authors and Affiliations

H.-S. Park
I. Son
Download PDF Download RIS Download Bibtex

Abstract

In this research, we investigated the effects of reduction atmospheres on the creation of the Mo-Si-B intermetallic compounds (IMC) during the heat treatments. For outstanding anti-oxidation and elevated mechanical strength at the ultrahigh temperature, we fabricated the uniformly dispersed IMC powders such as Mo5SiB2 (T2) and Mo3Si (A15) phases using the two steps of chemical reactions. Especially, in the second procedure, we studied the influence of the atmospheres (e.g. vacuum, argon, and hydrogen) on the synthesis of IMCs during the reduction. Furthermore, the newly produced IMCs were observed by SEM, XRD, and EDS to identify the phase of the compounds. We also calculated an amount of IMCs in the reduced powders depending on the atmosphere using the Reitveld refinement method. Consequently, it is found that hydrogen atmosphere was suitable for fabrication of IMC without other IMC phases.

Go to article

Authors and Affiliations

Jung Hyo Park
Seong Lee
Donghoon Kim
Youngmoo Kim
Sung Ho Yang
Sung Ho Lee
Download PDF Download RIS Download Bibtex

Abstract

We fabricated two different kinds of composite materials for absorbing microwave in a frequency range of 2 to 18 GHz using coaxial airline and thru-reflect-line (TRL) method. The composite materials having carbon nanotube (CNT) with carbonyl iron (CI) or iron oxide (Fe3O4) were fabricated by mixing each components. Magnetic properties were measured by SQUID equipment. Complex permittivity and complex permeability were also obtained by measuring S-parameters of the toroidal specimen dispersing CI/CNT and Fe3O4/CNT into the 50 weight percent (wt%) epoxy resin. The real permittivity was improved by mixing the CNT however, the real permeability was same as pure magnetic powders. The CI/CNT had a maximum value of real permittivity and real permeability, 11 and 1.4 at 10 GHz, respectively. The CNT composites can be adapted to the radar absorbing materials, band width 8-12 GHz.

Go to article

Authors and Affiliations

Jung Hyo Park
Jaeho Choi
Kisu Lee
Jinwoo Park
Jung Kun Song
Eunkyung Jeon
Download PDF Download RIS Download Bibtex

Abstract

This work presents the studies on the electrochemical process of thin palladium layers formation onto electrodeposited cobalt coatings. The suggested methodology consists of the preparation of thick and smooth cobalt substrate via galvanostatic electrodeposition. Cobalt coatings were prepared under different cathodic current density conditions from acidic bath containing cobalt sulphate and addition of boric acid. Obtained cobalt layers were analyzed by x-ray diffraction to determine their phase composition. Freshly prepared cobalt coatings were modificated by the galvanic displacement method in PdCl2 solution, to obtain smooth and compact Pd layer. The comparison of electrocatalytic properties of Co coatings with Co/Pd ones enabled to determine the influence of Palladium presence in cathodic deposits on the hydrogen evolution process.

Go to article

Authors and Affiliations

K. Skibińska
D. Kutyła
K. Kołczyk
A. Kwiecińska
R. Kowalik
P. Żabiński
Download PDF Download RIS Download Bibtex

Abstract

In this paper are presented results of study fusion characteristics of the biomass ashes from the hydrolyzed lignin and the ashes from the coke breeze. The hydrolyzed lignin ashes were compared with the coke breeze ashes i.e. with a fossil fuel. These ashes were prepared in muffle furnace at the temperature of 550°C (hydrolyzed lignin) and 850°C (coke breeze). Biomass (the hydrolyzed lignin) represents the new fuels for sintering process and an attractive way to decrease CO2 emissions from the energy production. The characterization methods were the following: standard fuel characterization analyses, chemical and mineralogical composition of the ashes and phase analyses of the ashes of biomass and the coke breeze. These ashes were prepared by the same method. Characterisation of the ashes samples was conducted by means of X-ray fluorescence (XRF), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Quantitative analysis of the crystalline and amorphous phases in each of the ash samples were carried out using the Rietveld method. The dominant phase of the ash from the coke breeze was mullite (Al6Si2O13). SiO2 is the dominant phase of the ash from the hydrolyzed lignin.

Go to article

Authors and Affiliations

M. Fröhlichová
R. Findorák
J. Legemza
M. Džupková
Download PDF Download RIS Download Bibtex

Abstract

The site preference of some transition metals during B2-type ordering has been investigated in the ternary Cu0.5(Zn1–xMx)0.5 alloys with M = Ti, V, Ag, Au, Cr, Mn, Fe, Co, Ni, Nb, Mo, Hf, Ta, W, Re or Pt (x ≤ 0.01). The statistic-o-thermodynamical theory combined with the electronic theory of alloys has been used to calculate the partial ordering energies, partial short range order parameters and the order-disorder transformation temperatures. The values of partial short range order parameters have been used to determine the site preference of the metal M. The analysis shows that the metals M can be divided into two groups with regard to lattice site occupancy. One group comprising of Cr, Mn, Fe, Co, Ni, Nb, Mo, Hf, Ta, W, Re or Pt was found to prefer Zn sublattice sites, while the second group of Ti, V, Ag or Au atoms prefer Cu sublattice sites. It is found that order-disorder transformation temperature and the site preference of metal M both depend strongly on the partial ordering energies and ternary alloying addition of metal M.

Go to article

Authors and Affiliations

N. Ahmad
A. B. Ziya
S. Atiq
K. Saifullah
M. Hashim
M. Saleem
Download PDF Download RIS Download Bibtex

Abstract

The effect of cobalt aluminate inoculant addition and melt-pouring temperature on the structure and mechanical properties of Ni-based superalloy was studied. The first major move to control the quality of investment cast blades and vanes was the control of grain size. Cobalt aluminate (CoAl2O4) is the most frequently utilized inoculant in the lost-wax casting process of Ni-based superalloys. The inoculant in the prime coat of moulds and pouring temperature play a significant role in grain size control. The finest surface grains were obtained when the internal surface of shell mould was coated with cobalt aluminate and subsequently pouring was at 1480°C. The influence of selected casting parameters and inoculant addition on mechanical properties was investigated on the basis of tensile, creep and hardness testing. The effect of grain refinement on mechanical properties were consistent with established theories. Tests conducted at ambient temperature indicated a beneficial effect of grain refinement both on tensile strength and hardness. In contrast at elevated temperature during creep, the reverse trend was observed.

Go to article

Authors and Affiliations

Ł. Rakoczy
M. Grudzień
R. Cygan
A. Zielińska-Lipiec
Download PDF Download RIS Download Bibtex

Abstract

Effects of additions of 0.00064, 0.001 and 0.0042 wt.% Bi on the graphite structure in the section thicknesses of 3, 12, 25, 38, 50, 75 and 100 mm of spheroidal graphite cast iron castings containing 2.11 wt.% Si and rare earth (RE) elements (Ce + La + Nd + Pr + Sm + Gd) in the range from 0.00297 to 0.00337 wt.% were analyzed in this paper. Addition of Bi was not necessary for obtaining high nodule count and nodularity higher than 80% in section thicknesses of 3, 12 and 25 mm. RE elements showed a beneficial effect on the nodule count and nodularity in these sections. Nodularity was below 80% in section thicknesses of 38, 50, 75 and 100 mm when Bi was not added. Detrimental effect of RE elements on graphite morphology in these sections was neutralized by adequate addition of Bi. Addition of 0.001 wt.% Bi (ratio of RE/Bi = 3.27) was enough to achieve nodularity above 80% in the section thickness of 38 mm. Nodularity was increased above 80% in section thicknesses of 50, 75 and 100 mm by addition of 0.0042 wt.% Bi (ratio of RE/Bi = 0.78). At the same time, Bi significantly increased the nodule count. Nodularity above 80% and the high nodule count in the section thicknesses of 75 and 100 mm were also achieved by using an external metallic chill in the mold. In this case, addition of Bi was not required.

Go to article

Authors and Affiliations

Z. Glavas
A. Strkalj
K. Maldini
F. Kozina
Download PDF Download RIS Download Bibtex

Abstract

Coagulation and solidification of the copper droplets suspend in the liquid slag are usually accompanied by the appearance of the Cu-Cu2O eutectic. Locally, this eutectic is created in the stationary state. Therefore, frequently it has a directional morphology. Since the E = (Zn) + Zn16Ti – eutectic is similar in the asymmetry of the phase diagram to the Cu-Cu2O – eutectic, the (Zn) single crystal strengthened by the E = (Zn) + Zn16Ti precipitate is subjected to directional growth by the Bridgman’s system and current analysis. Experimentally, the strengthening layers (stripes) are generated periodically in the (Zn) – single crystal as a result of the cyclical course of precipitation which accompanies the directional solidification. These layers evince diversified eutectic morphologies like irregular rods, regular lamellae, and regular rods. The L – shape rods of the Zn16Ti – intermetallic compound appear within the first range of the growth rates when the irregular eutectic structure is formed. Next, the branched rods transform into regular rods and subsequently the regular rods into regular lamellae transitions can be recorded. The regular lamellae exist only within a certain range of growth rates. Finally, the regular rods re-appear at some elevated growth rates. The entropy production per unit time and unit volume is calculated for the regular eutectic growth. It will allow to formulate the entropy production per unit time for both eutectic structure: rod-like and lamellar one.

Go to article

Authors and Affiliations

W. Wołczyński

Instructions for authors

Instructions for Authors


Archives of Metallurgy and Materials is a quarterly journal of Polish Academy of Sciences and Institute of Metallurgy and Materials Science PAS which publishes original scientific papers and reviews in the fields of metallurgy and materials science, foundry, mechanical working of metals, thermal engineering in metallurgy, thermodynamic and physical properties of materials, phase equilibria in the broad context and diffusion. In addition to the regular, original scientific papers and conference proceedings, invited reviews presenting the up-to-date knowledge and monothematic issues devoted to preferred areas of research will be published. Submission of a paper implies that it has not been published previously, that it is not under consideration for publication elsewhere, and that if accepted it will not be published elsewhere in the same form.


When preparing the manuscript, please pay attention to the following rules:


1. Manuscript submission

1.1. Manuscripts to be considered for publication should be submitted to the Editorial Office via www.editorialsystem.com/amm/. Authors should designate corresponding author, whose responsibility is to represent the Authors in contacts with the Editorial Office. The corresponding author receives an e-mail notification confirming the submission of the manuscript to the Editorial Office and is informed about the progress of the review process.


1.2. Manuscript should not exceed 15 pages of full-size paper (A4), must be double spaced (please use 12 point font), with generous margins, and the pages must be numbered. Authors should submit an electronic file of their manuscript in Microsoft Word (minimum : version 2000).


1.3. All manuscripts must be written in good English. Both British and U.S. English are acceptable but Authors should be consistent in their usage. It is sole responsibility of the Authors to make sure that the manuscript is grammatically correct and spell checked. Authors are strongly encouraged to have the manuscript proofread by a native speaker of English or a language professional, before it is submitted to the editorial office. Papers written in poor English will be automatically rejected without being subjected to review.


1.4. Authors should submit an electronic copy of final version of their paper in Microsoft Word Format, shemes (sketches) and figures saved as .eps, .jpeg, or .tiff.


1.5. Articles submitted for publication should include abstract and maximum 5 keywords.


1.6. Please adhere to the following order of presentation:


Author(s) with first names in full and ORCID.

Affiliation(s): in a short form (Institution, City, Country). Use the superscripts (*, **, . . .) after the Authors’ names in case of different affiliations.

Title: All words in lower case (first letter of first word capitalized).


Abstract: maximum 10 lines, including primary objective, research design, methods and procedures, main outcomes and results. Do not use abbreviations in the abstract.

Keywords: 5 maximum.

Main text: Begin on the second page with Introduction, followed by Experimental (Materials and Methods) and/or Theory section, Results, Discussion, and end with Conclusion section and Acknowledgement. When appropriate the Authors may choose to combine Results section and Discussion section into one Results and Discussion section. Make sure the text in sections is divided logically into paragraphs.
Use the decimal system for sections, subsections and (at the most) sub-subsections, as exemplified in the headings of these instructions.
All abbreviations should be spelled out the first time they are introduced in text or references. Thereafter the abbreviation can be used.


Appendices

References

Correspondence address: title, name, postal address, telephone and e-mail address of the corresponding Author, number ORCID.

Figure captions

Tables

2. Manuscript preparation


The editorial system includes:


1. Manuscript, which should contain the full text with figures, tables and signatures to them where they are placed.


2. Figures, tables and signatures to them as separate files.


2.1. Formulae, equations and units
The formulas should be written in Microsoft Equation and MathType with the possibility of editing (not as graphics).
Formulae and equations should be typed on separate lines and numbered consecutively in parentheses on the right side (1) . . . (n). Vectors must be indicated as such. Size of symbols should be kept uniform for all equations in the manuscript. Formulae and equations should be referred to in the text as follows: Eq. (1).
Numbers and units must be separated by a space, e.g. 5.5 wt.%, 273.15 K, 1013 MPa, etc. The only exception are angle degrees, e.g. 90°.

2.2. Figures

Figures should be complete without corrections and additions in the word. Figures are usually printed in reduced size (fitting column width of 85 mm) and this should be taken into account when preparing them. For the best results, make sure that lettering on figures and micrographs is at least 2 mm high after reduction, and the style of labeling must be uniform for all figures. Each figure should have its own caption explaining the content without reference to the text. Figure captions should be typed on a separate page at the end of manuscript. The appropriate place of in the text should be indicated by <Fig. 3 > written in separate line. Figures should be referred to in text as follows: Fig. 1. The magnification must be indicated by a labeled scale marker on the micrograph itself, not drawn below it. For optimum printing quality micrographs should be saved as .eps or .tiff at a resolution of at least 300 dpi while line drawings at a resolution of at least 600 dpi.

2.3. Move file
The authors can make movie files up to 100 MB in MP4 format.
The author at the first reference (Movie 1. Click here) should with the Click here command connect the web address with the place of uploading the movie (hyperlink) and at the end of the article provide a list of hyperlinks (samples: Movie 1, hyperlink, movie no 2, hyperlink ......).

The files will be removed from the edytorial system when rejected or published article (moved to Rejected or Published manuscripts).


2.4. Tables

Tables together with captions should be typed on separate page at the end of manuscript. Tables are to be numbered consecutively using Arabic numbers in the text (TABLE 1 . . . n). A caption must be placed above respective table and should explain the symbols used in the heading and in the left hand column. Tables should be referred to in the text as follows: TABLE 1.


2.5. References

References should be typed on separate pages and numbered consecutively applying the system accepted by the Quarterly (initials and names all authors, journal title [abbreviated according to the Journal Title Abbreviations of Web of Science: http://library.caltech.edu/reference/abbreviations/, everyone abbreviation should be end with a dot - example. Arch.Metall.Mater.] or book title; journal volume or book publisher; page spread; publication year in bracket).

The use of DOI numbers (full notation and linked) is mandatory for each paper and should be formatted as shown in the examples below:

Journals:

[1] L.B. Magalas, Development of High-Resolution Mechanical Spectroscopy, HRMS: Status and Perspectives. HRMS Coupled with a Laser Dilatometer. Arch. Metall. Mater. 60 (3), 2069-2076 (2015). DOI: https://doi.org/10.1515/AMM-2015-0350

[2] E. Pagounis, M.J. Szczerba, R. Chulist, M. Laufenberg, Large Magnetic Field-Induced Work output in a NiMgGa Seven-Lavered Modulated Martensite. Appl. Phys. Lett. 107, 152407 (2015). DOI: https://doi.org/10.1063/1.4933303

[3] H. Etschmaier, H. Torwesten, H. Eder, P. Hadley, Suppression of Interdiffusion in Copper/Tin thin Films. J. Mater. Eng. Perform. (2012).DOI: https://doi.org/10.1007/s11665-011-0090-2 (in press).

Books:

[2] M. H. Kamdar, A.M.C. Westwood, Environment-Sensitive Mechanical Behaviour, New York 1981.

Proceedings:

[3] F. Erdogan, in: H. Liebowitz (Ed.), Fracture 2, Academic Press 684, New York (1968).

Internet resource:

[4] http://www.twi.co.uk/content/fswqual.html

PhD Thesis:

[6] F.M. LIang. World Hyphenation by Computer. PhD thesis, Stanford University, Stanford, CA 94305, June.

Chapter in books:

[7] R. Major, P. Lacki, R. Kustosz, J. M. Lackner, Modelling of nanoindentation to simulate thin layer behavior, in: K. J. Kurzydłowski, B. Major,

P. Zięba (Ed.), Foundation of Materials Design 2006, Research Signpost (2006).

Articles in press:

[8] H. EtschmaIer, H. Torwesten, H. Eder, P. Hadley, J. Mater. Eng. Perform. (2012), DOI: 10.1007/s11665-011-0090-2 (in press).

3. Fees

No honorarium will be paid. The journal does not have article processing charges (APCs) nor article submission charges.

4. Review and proofread process

4.1. Peer review process All submitted manuscripts undergo review by renowned specialists appointed by the Editor-in-Chief and members of the Editorial Board. Reviewers receive guidance to help them perform the review, and submit written opinion on the manuscript together with recommendation to accept as is, or reject, or accept after revision. In the latter case i.e. when revision is requested, the authors are obliged to respond to Editor and Reviewers’ comments in detail and make revisions to the manuscript. A rebuttal to Reviewers’ comments can also be sent via the Editorial System in writing. Decision to reject the article is taken by the Editorial Board with the final decision belonging to the Editor, who may appoint another reviewer if necessary. Reviewers remain anonymous to Authors and their identity cannot be revealed by the Editorial Office.

In a separate file, the authors are requested to suggest names and contact details (affiliations and valid e-mail addresses) of at least three experts who could serve as reviewers.

Brief explanation (2-3 sentence-long) why each person is suitable as a reviewer should also be provided. The suggested reviewers cannot be from the same country as affiliation of the corresponding author. The decision to appoint a reviewer belongs solely to the editor.

4.2. Revised manuscript submission

When revision of a manuscript is requested, Authors should return the revised version of their manuscript as soon as possible. Prompt action may ensure fast publication if a paper is finally accepted for publication in Arch. Metall. Mater. If it is the first revision of an article Authors are requested to return their revised manuscript within 7 days.

If it is the second revision Authors are requested to return their revised manuscript within 1 day.

4.3. Final proofreading

Authors will receive a pdf file with the edited version of their manuscript for final proofreading. This is the last opportunity to view an article before its publication on the journal web site. No changes or modifications can be introduced once it is published. Thus authors are requested to check their proof pages carefully against manuscript within 3 working days and prepare a separate document containing all changes that should be introduced. Authors are sometimes asked to provide additional comments and explanations in response to remarks and queries from the language or technical editors.

5. Original version

Starting from issue 1/ 2018, Volume 63, Archives of Metallurgy and Materials is published in electronic via www.journals.pan.pl. The printed version is printed only for designated libraries (legal basis: Regulation of the Minister of Culture and Art of March 6, 1997).

6. Prevent cases of plagiarism

Readers should be sure that the authors present the results of their work transparently, fair and honest, regardless of whether they are the direct authors, or used the help of a specialized entity (natural or legal person). To prevent cases of plagiarism, "ghostwriting" and "guest Authorship", the Editorial Office will require that the Authors disclosed the contribution of individual Authors in the creation of manuscript (with their affiliations and contributions, i.e. the information who is responsible for: research concept and design, collection and/or assembly of data, data analysis and interpretation, writing the manuscript). Funding sources (together with grant number) must also be revealed. The corresponding Author will bear the main responsibility for the manuscript. Detected cases will be exposed, including notifying the appropriate entities (institutions employing the Authors, scientific societies, associations of editors of scientific journals, etc.).

7. License type

Articles are printed in an open access and distributed under the terms of the Creative Commons Attribution-NonCommercial (CC BY-NC 4.0, https://creativecommons.org/licenses/by-nc/4.0/). This license allows authors to copy and redistribute the material in any medium or format, remix, transform, and build upon the material. Authors may not use the material for commercial purposes. However, this condition does not include dependent works (they may be covered by another license).

Submission of an article to the journal is unequivocal to expressing consent to the publication in both paper and electronic form.

Additional info

Archives of Metallurgy and Materials is covered by the following services:


Arianta, Baidu Scholar, BazTech, Celdes, Chemical Abstracts Service (CAS) - CAplus, Clarivate Analytics (formerly Thomson Reuters) - Current Contents/Engineering, Computing, and Technology, Clarivate Analytics (formerly Thomson Reuters) - Journal Citation Reports/Science Edition, Clarivate Analytics (formerly Thomson Reuters) - Materials Science Citation Index, Clarivate Analytics (formerly Thomson Reuters) - Science Citation Index Expanded, CNKI Scholar (China National Knowledge Infrastructure), CNPIEC, DOAJ (Directory of Open Access Journals), EBSCO (relevant databases), EBSCO Discovery Service, Elsevier - SCOPUS, Genamics JournalSeek, Google Scholar, Index Copernicus, J-Gate, JournalTOCs, KESLI-NDSL (Korean National Discovery for Science Leaders), Microsoft Academic, Naviga (Softweco), Primo Central (ExLibris), ProQuest (relevant databases), ReadCube, ResearchGate, SCImago (SJR), Sherpa/RoMEO, Summon (Serials Solutions/ProQuest), TDNet, TEMA Technik und Management, Ulrich's Periodicals Directory/ulrichsweb, WanFang Data, WorldCat (OCLC)

This page uses 'cookies'. Learn more